Technical Datasheet(English) 

PA6

Food Contact

Low viscosity

Injection

BMW GS 93016

Mercedes-Benz DBL 5403.00

Mercedes-Benz DBL 5410.00

VAG(Volkswagen Group) VW 50125

VAG(Volkswagen Group) VW 50134

Stress-strain -40|%|Mpa|Strain in %|Stress in MPa|0:0@0.00874:0.57689@0.03225:1.36109@0.05208:2.10821@0.07494000000000001:2.85781@0.10966:4.01917@0.13126:4.78328@0.15354:5.54156@0.17473:6.27231@0.19585:7.01361@0.21691:7.76539@0.25052:8.874000000000001@0.4939:17.33488@0.90965:31.40694@1.31169:44.63393@1.71594:57.22973@1.99314:65.47717@2.42046:77.25682999999999@2.84888:87.92102@3.14779:94.35339999999999@3.45519:100.12971@3.77252:105.16174@4.10185:109.44469@4.4421:112.93626@4.79867:115.65071@5.16826:117.69628@5.74469:119.61978@6.34816:120.54334@6.96218:120.74177{n}23|%|Mpa|Strain in %|Stress in MPa|0:0@0.02334:0.93211@0.05725:2.02274@0.079:2.74055@0.11364:3.83583@0.14666:4.91222@0.17003:5.64313@0.19059:6.3396@0.21408:7.06461@0.23799:7.7953@0.30836:9.90986@0.58982:19.25964@0.99576:32.28066@1.40334:44.77246@1.81802:56.76697@2.24699:67.89962@2.54297:74.45505@2.85421:80.01472@3.19001:84.22383000000001@3.56004:86.73023000000001@3.97594:87.47841@4.65693:86.49196999999999{n}100|%|Mpa|Strain in %|Stress in MPa|0:0@0.15794:1.07382@2.07925:10.28261@3.39026:14.49321@6.09043:20.24525@8.87904:23.81666@11.74868:26.07613@14.70377:27.51875@17.73812:28.45401@20.80198:29.0674{n}150|%|Mpa|Strain in %|Stress in MPa|0:0@0.14:0.43@0.55:2.09@1.24:4.9@2.2:8.18@3.44:11.48@4.95:14.41@6.74:16.78@8.800000000000001:18.56@11.14:19.79@13.75:20.65@16.64:21.23@19.81:21.63@23.24:21.88@26.96:21.99@30.95:21.87

Stress-strain (Cond.)(Yield) 23|%|Mpa|Strain in %|Stress in MPa|0:0@0.15:1.17@0.59:6.02@1.32:13.33@2.34:20.15@3.66:25.34@5.27:29.54@7.17:33.44@9.369999999999999:37.12@11.86:40.33@14.64:42.83@17.71:44.52@21.08:45.44@24.74:45.75@28.69:45.61

Secant modulus-strain 23|%|MPa|Strain in %|Secant modulus in MPa|1.36:3019.85294@1.95:2936.41026@2.66:2747.74436@3.47:2415.56196@4.39:1960.82005@5.42:1545.75646@6.56:1226.21951@7.81:998.07939@9.17:817.33915@10.63:538.94638@12.2:422.62295@13.89:371.2023@15.68:326.40306@17.57:293.22709@19.58:257.30337{n}100|%|MPa|Strain in %|Secant modulus in MPa|1.22:527.86885@2.17:484.79263@3.39:430.67847@4.88:375.81967@6.64:325.90361@8.67:281.31488@10.98:241.62113@13.55:207.38007@16.4:177.9878@19.52:153.27869@22.91:132.7368@26.57:115.61912@30.5:101.34426@34.7:89.36599@39.17:79.24432@43.92:70.67395@48.93:63.37625{n}150|%|MPa|Strain in %|Secant modulus in MPa|1.24:395.16129@2.2:371.81818@3.44:333.72093@4.95:291.11111@6.74:248.96142@8.800000000000001:210.90909@11.14:177.64811@13.75:150.18182@16.64:127.58413@19.81:109.18728@23.24:94.14802@26.96:81.56528@30.95:70.66236000000001@35.21:59.69895@39.75:53.2327@44.56:47.5763@49.65:42.71903

Secant modulus-strain (Cond.) 23|%|MPa|Strain in %|Secant modulus in MPa|1.32:1009.84848@2.34:861.1111100000001@3.66:692.34973@5.27:560.53131@7.17:466.38773@9.369999999999999:396.15795@11.86:340.05059@14.64:292.55464@17.71:251.3834@21.08:215.55977@24.74:184.9232@28.69:158.97525@32.93:136.34983@37.47:109.50093@42.3:91.77305@47.42:82.68662999999999@52.84:74.24299999999999

Viscosity-shear rate 240|1/s|Pa s|Shear rate in 1/s|Viscosity in Pa s|1:194.68835@10:193.67521@20:192.68723@50:190.02217@100:186.06837@200:179.1361@500:162.49185@1000:142.19397@2000:115.38648@5000:75.99576999999999@10000:49.85035@20000:30.39906@50000:14.66586@100000:8.169739999999999{n}260|1/s|Pa s|Shear rate in 1/s|Viscosity in Pa s|1:113.54327@10:113.1779@20:112.82019@50:111.8483@100:110.38732@200:107.76921@500:101.172@1000:92.47485@2000:79.72783@5000:57.81658@10000:40.65216@20000:26.19083@50000:13.24084@100000:7.52474{n}280|1/s|Pa s|Shear rate in 1/s|Viscosity in Pa s|1:71.48374@10:71.33156@20:71.18225@50:70.77494@100:70.15818@200:69.03921@500:66.13903000000001@1000:62.1293@2000:55.83372@5000:43.66813@10000:32.71625@20000:22.30982@50000:11.90164@100000:6.93266

Shearstress-shear rate 220|1/s|Pa|Shear rate in 1/s|Shearstress in Pa|389:185000@1250:342000@3900:545000@8570:728000@24800:950000@54200:1100000{n}260|1/s|Pa|Shear rate in 1/s|Shearstress in Pa|1040:195000@2620:318000@11800:599000@34000:819000@62100:944000{n}300|1/s|Pa|Shear rate in 1/s|Shearstress in Pa|3750:219000@7590:340000@14200:463000@24300:557000@46800:695000@70400:795000@82200:835000

Dynamic Shear modulus (G storage)-temperature |°C|MPa|Temperature in °C|G' in MPa|-0.96:1210@10.48:1200@20.22:1190@30.91:1170@39.57:1160@45.5:1130@48.2:1080@50.16:1000@52.11:894@54.53:746@56.04:658@57.28:601@60.43:490@63.64:416@67.20999999999999:356@71.94:299@79.53:243@89.94:204@100.32:186@110.38:177@120.44:171@130.41:165@140.07:159@150.04:151@160.09:144@170.16:135@180.11:123@190.29:105@200.35:75.8@210.29:40@222:0.498

Stress-strain (isochronous)(Creep) 23°C(Break) 1|%|MPa|Strain in %|Stress in MPa|0:0@0.17:5@0.34:10@0.5:15@0.6899999999999999:20@0.88:25@1.08:30@1.31:35@1.57:40@2:47.2@2.5:53{n}10|%|MPa|Strain in %|Stress in MPa|0:0@0.19:5@0.38:10@0.5600000000000001:15@0.75:20@0.95:25@1.2:30@1.5:35@1.82:40@2.5:47.8@3:52.1{n}100|%|MPa|Strain in %|Stress in MPa|0:0@0.21:5@0.42:10@0.64:15@0.86:20@1.12:25@1.45:30@1.82:35@2.24:40@3:46.5{n}1000|%|MPa|Strain in %|Stress in MPa|0:0@0.27:5@0.53:10@0.78:15@1.07:20@1.44:25@1.85:30@2.3:35@2.89:40@3:40.7{n}10000|%|MPa|Strain in %|Stress in MPa|0:0@0.33:5@0.65:10@0.97:15@1.36:20@1.85:25@2.33:30@2.93:35@3:35.5

Stress-strain (isochronous)(Creep) 23°C (cond.)(Break) 1|%|MPa|Strain in %|Stress in MPa|0:0@0.11:1@0.23:2@0.36:3@0.51:4@0.66:5@0.85:6@1.02:7@1.22:8@1.41:9@1.95:11{n}10|%|MPa|Strain in %|Stress in MPa|0:0@0.125:1@0.26:2@0.42:3@0.57:4@0.75:5@0.97:6@1.16:7@1.4:8@1.65:9@2.3:11{n}100|%|MPa|Strain in %|Stress in MPa|0:0@0.147:1@0.31:2@0.49:3@0.67:4@0.87:5@1.12:6@1.37:7@1.65:8@1.96:9@2.73:11{n}1000|%|MPa|Strain in %|Stress in MPa|0:0@0.175:1@0.37:2@0.58:3@0.78:4@1.02:5@1.3:6@1.59:7@1.91:8@2.28:9@3.17:11{n}10000|%|MPa|Strain in %|Stress in MPa|0:0@0.21:1@0.46:2@0.68:3@0.93:4@1.2:5@1.53:6@1.9:7@2.26:8@2.69:9@3.76:11

Stress-strain (isochronous)(Creep) 40°C(Break) 1|%|MPa|Strain in %|Stress in MPa|0:0@0.13:2.5@0.28:5@0.43:7.5@0.59:10@0.76:12.5@0.93:15@1.1:17.5@1.27:20@1.48:22.5{n}10|%|MPa|Strain in %|Stress in MPa|0:0@0.18:2.5@0.39:5@0.62:7.5@0.8100000000000001:10@1.04:12.5@1.25:15@1.49:17.5@1.7:20@2.14:22.5{n}100|%|MPa|Strain in %|Stress in MPa|0:0@0.26:2.5@0.58:5@0.88:7.5@1.15:10@1.46:12.5@1.77:15@2.18:17.5{n}1000|%|MPa|Strain in %|Stress in MPa|0:0@0.38:2.5@0.8:5@1.23:7.5@1.62:10@2.03:12.5@2.49:15{n}10000|%|MPa|Strain in %|Stress in MPa|0:0@0.52:2.5@1.08:5@1.68:7.5@2.27:10@2.9:12.5

Stress-strain (isochronous)(Creep) 60°C(Break) 1|%|MPa|Strain in %|Stress in MPa|0:0@0.12:1@0.25:2@0.39:3@0.51:4@0.66:5@0.8100000000000001:6@0.97:7@1.12:8@1.27:9@1.42:10{n}10|%|MPa|Strain in %|Stress in MPa|0:0@0.146:1@0.3:2@0.46:3@0.6:4@0.77:5@0.97:6@1.15:7@1.32:8@1.5:9@1.7:10{n}100|%|MPa|Strain in %|Stress in MPa|0:0@0.169:1@0.35:2@0.52:3@0.71:4@0.9:5@1.11:6@1.31:7@1.5:8@1.7:9@1.92:10{n}1000|%|MPa|Strain in %|Stress in MPa|0:0@0.195:1@0.4:2@0.6:3@0.82:4@1.04:5@1.26:6@1.47:7@1.71:8@1.95:9@2.2:10{n}10000|%|MPa|Strain in %|Stress in MPa|0:0@0.229:1@0.47:2@0.7:3@0.95:4@1.18:5@1.4:6@1.67:7@1.93:8@2.17:9@2.46:10

Stress-strain (isochronous)(Creep) 100°C(Break) 1|%|MPa|Strain in %|Stress in MPa|0:0@0.182:1@0.389:2@0.61:3@0.845:4@1.08:5@1.32:6@1.57:7{n}10|%|MPa|Strain in %|Stress in MPa|0:0@0.21:1@0.455:2@0.72:3@1:4@1.29:5@1.6:6

Creep modulus-time 23°C (cond.) 1|h|MPa|Time in h|Creep modulus in MPa|1:909@10:800@100:680@1000:571@10000:476{n}2|h|MPa|Time in h|Creep modulus in MPa|1:870@10:769@100:645@1000:541@10000:435{n}3|h|MPa|Time in h|Creep modulus in MPa|1:833@10:714@100:612@1000:517@10000:441{n}4|h|MPa|Time in h|Creep modulus in MPa|1:784@10:702@100:597@1000:513@10000:430{n}5|h|MPa|Time in h|Creep modulus in MPa|1:758@10:667@100:575@1000:490@10000:417{n}6|h|MPa|Time in h|Creep modulus in MPa|1:706@10:619@100:536@1000:462@10000:392{n}7|h|MPa|Time in h|Creep modulus in MPa|1:686@10:603@100:511@1000:440@10000:368{n}8|h|MPa|Time in h|Creep modulus in MPa|1:656@10:571@100:485@1000:419@10000:354{n}9|h|MPa|Time in h|Creep modulus in MPa|1:638@10:545@100:459@1000:395@10000:335{n}11|h|MPa|Time in h|Creep modulus in MPa|1:564@10:478@100:403@1000:347@10000:293

Creep modulus-time 40°C 2.5|h|MPa|Time in h|Creep modulus in MPa|1:1920@10:1390@100:962@1000:658@10000:481{n}5|h|MPa|Time in h|Creep modulus in MPa|1:1790@10:1280@100:862@1000:625@10000:463{n}7.5|h|MPa|Time in h|Creep modulus in MPa|1:1740@10:1210@100:852@1000:610@10000:446{n}10|h|MPa|Time in h|Creep modulus in MPa|1:1690@10:1230@100:870@1000:617@10000:441{n}12.5|h|MPa|Time in h|Creep modulus in MPa|1:1640@10:1200@100:856@1000:616@10000:431

Creep modulus-time 60°C 1|h|MPa|Time in h|Creep modulus in MPa|1:833@10:685@100:592@1000:513@10000:437{n}2|h|MPa|Time in h|Creep modulus in MPa|1:800@10:667@100:571@1000:500@10000:426{n}3|h|MPa|Time in h|Creep modulus in MPa|1:769@10:652@100:577@1000:500@10000:429{n}4|h|MPa|Time in h|Creep modulus in MPa|1:784@10:667@100:563@1000:488@10000:421{n}5|h|MPa|Time in h|Creep modulus in MPa|1:758@10:649@100:556@1000:481@10000:424{n}6|h|MPa|Time in h|Creep modulus in MPa|1:741@10:619@100:541@1000:476@10000:429{n}7|h|MPa|Time in h|Creep modulus in MPa|1:722@10:609@100:534@1000:476@10000:419{n}8|h|MPa|Time in h|Creep modulus in MPa|1:714@10:606@100:533@1000:468@10000:415{n}9|h|MPa|Time in h|Creep modulus in MPa|1:709@10:600@100:529@1000:462@10000:415{n}10|h|MPa|Time in h|Creep modulus in MPa|1:704@10:588@100:521@1000:455@10000:407

Specific volume-temperature (pvT) 0|°C|E-3 m³/kg|Spec. volume in °C|Temperature in E-3 m³/kg|20:0.86389@40:0.87073@60:0.87761@80:0.88458@100:0.89174@120:0.8993100000000001@130:0.9034@140:0.90782@150:0.91274@160:0.91842@170:0.9252@180:0.93366@190:0.9446099999999999@200:0.95927@210:0.97949@220:1.008@230:1.01499@236:1.01859@238:1.01979@242:1.02218@262:1.03417@282:1.04615@302:1.05813@322:1.07012@342:1.0821{n}40|°C|E-3 m³/kg|Spec. volume in °C|Temperature in E-3 m³/kg|20:0.85741@40:0.8638400000000001@60:0.87027@80:0.87675@100:0.88335@120:0.89027@130:0.89396@140:0.8979200000000001@150:0.90228@160:0.90724@170:0.9131@180:0.92031@190:0.92954@200:0.9418@210:0.95858@220:0.9821@230:0.99294@236:0.99605@238:0.99709@242:0.99916@262:1.00946@282:1.01965@302:1.02973@322:1.03968@342:1.04952{n}80|°C|E-3 m³/kg|Spec. volume in °C|Temperature in E-3 m³/kg|20:0.85143@40:0.85751@60:0.86356@80:0.86963@100:0.87577@120:0.88214@130:0.88551@140:0.88909@150:0.89299@160:0.89737@170:0.90247@180:0.90868@190:0.91652@200:0.92682@210:0.9408@220:0.96027@230:0.97521@236:0.97801@238:0.97894@242:0.9807900000000001@262:0.98999@282:0.99903@302:1.00791@322:1.01663@342:1.02518{n}120|°C|E-3 m³/kg|Spec. volume in °C|Temperature in E-3 m³/kg|20:0.84589@40:0.85165@60:0.85738@80:0.86309@100:0.86885@120:0.87477@130:0.87787@140:0.88113@150:0.88465@160:0.88855@170:0.8930399999999999@180:0.89842@190:0.90513@200:0.91384@210:0.92554@220:0.94171@230:0.96038@236:0.96295@238:0.9638@242:0.9655@262:0.9739100000000001@282:0.98214@302:0.99019@322:0.99807@342:1.00576{n}160|°C|E-3 m³/kg|Spec. volume in °C|Temperature in E-3 m³/kg|20:0.84072@40:0.84621@60:0.85165@80:0.85706@100:0.86248@120:0.86802@130:0.8708900000000001@140:0.8738899999999999@150:0.87709@160:0.8806@170:0.88459@180:0.88929@190:0.89507@200:0.9024799999999999@210:0.91231@220:0.92579@230:0.94472@236:0.95003@238:0.95083@242:0.95241@262:0.96021@282:0.96784@302:0.97528@322:0.98253@342:0.98959{n}200|°C|E-3 m³/kg|Spec. volume in °C|Temperature in E-3 m³/kg|20:0.83587@40:0.84112@60:0.84631@80:0.85146@100:0.85659@120:0.8618@130:0.86448@140:0.86725@150:0.87019@160:0.87338@170:0.8769400000000001@180:0.88109@190:0.88611@200:0.89244@210:0.90076@220:0.91203@230:0.92775@236:0.93872@238:0.93947@242:0.94096@262:0.94829@282:0.95544@302:0.96239@322:0.96916@342:0.9757400000000001

Dynamic Shear modulus-temperature G'|°C|MPa|Temperature in °C|Dyn. Shear modulus in MPa|-0.96:1210@10.48:1200@20.22:1190@30.91:1170@39.57:1160@45.5:1130@48.2:1080@50.16:1000@52.11:894@54.53:746@56.04:658@57.28:601@60.43:490@63.64:416@67.20999999999999:356@71.94:299@79.53:243@89.94:204@100.32:186@110.38:177@120.44:171@130.41:165@140.07:159@150.04:151@160.09:144@170.16:135@180.11:123@190.29:105@200.35:75.8@210.29:40@222:0.498{n}G"|°C|MPa|Temperature in °C|Dyn. Shear modulus in MPa|-0.96:3.8962@10.48:4.02@20.22:5.4502@30.91:7.6401@39.57:10.4864@45.5:16.7692@48.2:27.3024@50.16:43.51@52.11:64.3322@54.53:84.4024@56.04:91.1001@57.28:92.12730000000001@60.43:85.10809999999999@63.64:73.5821@67.20999999999999:60.7158@71.94:46.7038@79.53:30.7784@89.94:18.0703@100.32:11.8408@110.38:9.267720000000001@120.44:8.06265@130.41:7.4382@140.07:7.05165@150.04:6.62739@160.09:6.25248@170.16:5.85495@180.11:5.45751@190.29:5.2101@200.35:4.89365@210.29:3.5488@222:0.18273{n}tan d|°C|MPa|Temperature in °C|Dyn. Shear modulus in MPa|-0.96:0.00322@10.48:0.00335@20.22:0.00458@30.91:0.00653@39.57:0.009039999999999999@45.5:0.01484@48.2:0.02528@50.16:0.04351@52.11:0.07196@54.53:0.11314@56.04:0.13845@57.28:0.15329@60.43:0.17369@63.64:0.17688@67.20999999999999:0.17055@71.94:0.1562@79.53:0.12666@89.94:0.08858000000000001@100.32:0.06365999999999999@110.38:0.05236@120.44:0.04715@130.41:0.04508@140.07:0.04435@150.04:0.04389@160.09:0.04342@170.16:0.04337@180.11:0.04437@190.29:0.04962@200.35:0.06456000000000001@210.29:0.08871999999999999@222:0.36693

Creep modulus-time 23°C 10|h|MPa|Time in h|Creep modulus in MPa|1:2941.18@10:2631.58@100:2380.95@1000:1886.79@10000:1538.46{n}20|h|MPa|Time in h|Creep modulus in MPa|1:2898.55@10:2666.67@100:2325.58@1000:1869.16@10000:1470.59{n}30|h|MPa|Time in h|Creep modulus in MPa|1:2777.78@10:2500@100:2068.97@1000:1621.62@10000:1287.55{n}40|h|MPa|Time in h|Creep modulus in MPa|1:2547.77@10:2197.8@100:1785.71@1000:1384.08{n}47|h|MPa|Time in h|Creep modulus in MPa|1:2367.44@10:1945.52