| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Density/Specific Gravity |
*** g/cm³
| ISO 1183 | |
Melt Mass Flow Rate(MFR) | | | |
190℃/1.05 kg |
*** g/10min | ASTM D1238 | |
Water Absorption |
*** %
| ISO 62 | 23℃,24 hr immersion |
Water Absorption |
*** %
| ISO 62 | 23℃,Equilibrium, 50% RH |
Water Absorption |
*** %
| ISO 62 | 23℃,Equilibrium, lmmersion |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus |
*** Mpa
| ISO 527 | 23℃, 5.1mm/min |
Tensile Strength | | | |
- |
*** Mpa | ISO 527 | -55℃, 5.1mm/min |
- |
*** Mpa | ISO 527 | 100℃, 5.1mm/min |
- |
*** Mpa | ISO 527 | 121℃, 5.1mm/min |
- |
*** Mpa | ISO 527 | 23℃, 5.1mm/min |
- |
*** Mpa | ISO 527 | 70℃, 5.1mm/min |
Tensile Elongation | | | |
Break |
*** % | ISO 527 | -55℃, 5.1mm/min |
Break |
> *** % | ISO 527 | 100℃, 5.1mm/min |
Break |
> *** % | ISO 527 | 121℃, 5.1mm/min |
Break |
*** % | ISO 527 | 23℃, 5.1mm/min |
Break |
*** % | ISO 527 | 70℃, 5.1mm/min |
Flexural Modulus |
*** Mpa
| ISO 178 | -55℃, 5.1mm/min |
Flexural Modulus |
*** Mpa
| ISO 178 | 100℃, 5.1mm/min |
Flexural Modulus |
*** Mpa
| ISO 178 | 121℃, 5.1mm/min |
Flexural Modulus |
*** Mpa
| ISO 178 | 23℃, 5.1mm/min |
Flexural Modulus |
*** Mpa
| ISO 178 | 70℃, 5.1mm/min |
Flexural Strength | | | |
Yield |
*** Mpa | ISO 178 | 23℃, 1.3mm/min |
Poisson Ratio |
*** -
| - | |
Coefficient of Friction |
*** -
| ASTM D 3702 | Dynamic |
Coefficient of Friction |
*** -
| ASTM D 3702 | Static |
Shear Strength |
*** Mpa
| ASTM D 732 | 23℃ |
Flexural Fatigue |
*** Mpa
| ASTM D671 | 50%RH, 23℃, 1E+6 Cycles |
Compressive Strength |
*** Mpa
| ISO 604 | 23℃ at 1% Def. |
Compressive Strength |
*** Mpa
| ISO 604 | 23℃ at 10% Def. |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Izod Notched Impact Strengh | | | |
-40℃ (-40℉) |
*** kJ/m² | ISO 180/1A | |
23℃ (73℉) |
*** kJ/m² | ISO 180/1A | |
Izod Unnotched Impact Strengh | | | |
23℃ (73℉) |
*** kJ/m² | ISO 180 | |
Tensile Impact |
*** kJ/m²
| ISO 8256 | 23℃ |
| Hardness | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Rockwell M |
*** M
| ISO 2039 | |
Rockwell R |
*** R
| ISO 2039 | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | | | |
0.45 Mpa (66 psi)（4.6kg/cm²） |
*** °C | ISO 75 | |
1.8 Mpa (264 psi)（18.6kg/cm²） |
*** °C | ISO 75 | |
Coefficient of Linear Thermal Expansion | | | |
- |
*** E-6/°C | ASTM D 696 | -40 to 29℃ |
- |
*** E-6/°C | ASTM D 696 | 104 to 149℃ |
- |
*** E-6/°C | ASTM D 696 | 29 to 60℃ |
- |
*** E-6/°C | ASTM D 696 | 60 to 104℃ |
Melt Temperature(Tm) |
*** °C
| ISO 3146 | |
Thermal Conductivity |
*** W/(m K)
| - | |
Deformation |
*** %
| ASTM D621 | 13.8Mpa, 50℃ |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Flame Rating | | | |
HB |
*** mm | UL94 | |
| Electrical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Volume Resistivity |
*** Ohm-cm
| IEC 60093 | 23℃, at 2% water |
Dielectric Constant(Permittivity) | | | |
1MHz |
*** - | IEC 60250 | 50%RH, 23℃ |
Dissipation Factor | | | |
1MHz |
*** E-4 | IEC 60250 | 50%RH, 23℃ |
Dielectric Strength |
*** kV/mm
| IEC 60243 | short time, 2.3mm |
Arc Resistance |
*** sec
| ASTM D495 | |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.