Delrin® 900P is a general purpose low viscosity acetal homopolymer for multicavity and thin wall moulding with improved processing thermal stability and low VOC emissions.
| Original Document | Technical Datasheet(English) | |||
| Solutions | Gears | |||
| Resin ID | POM | |||
| Features | Low EmissionLow viscosityHomopolymer | |||
| Additive | Release AgentLubricant | |||
| Applications | Thin wall injection moldingMulti cavity moulding | |||
| Appearance | Pellets/GranulesNatural Color | |||
| Processing | Injection | |||
| Diagrams | Viscosity-shear rateShearstress-shear rateDynamic Shear modulus (G storage)-temperatureStress-strain(Yield)Secant modulus-strain(Yield)Specific volume-temperature (pvT) | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | |
Melt Volume Flow Rate(MVR) | |||
190℃/2.16 kg | *** cm³/10min | ISO 1133 | |
Melt Mass Flow Rate(MFR) | |||
190℃/2.16 kg | *** g/10min | ISO 1133 | |
Mold Shrinkage | |||
Flow | *** % | ISO 294-4, 2577 | |
Across Flow | *** % | ISO 294-4, 2577 | |
Water Absorption | *** % | ISO 62 | 2mm |
Moisture /Humidity Absorption | *** % | ISO 62 | 2mm |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ISO 527-1/-2 | |
Tensile Strength | |||
Yield | *** Mpa | ISO 527-1/-2 | |
Tensile Elongation | |||
Yield | *** % | ISO 527-1/-2 | |
Nominal Tensile Strain at Break | *** % | ISO 527-1/-2 | |
Flexural Modulus | *** Mpa | ISO 178 | |
Tensile Creep Modulus | |||
1h | *** Mpa | ISO 899-1 | |
1000h | *** Mpa | ISO 899-1 | |
Poisson Ratio | *** - | - | |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 179/1eA | |
23℃ (73℉) | *** kJ/m² | ISO 179/1eA | |
Charpy Unnotched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 179/1eU | |
23℃ (73℉) | *** kJ/m² | ISO 179/1eU | |
Izod Notched Impact Strengh | |||
-40℃ (-40℉) | *** kJ/m² | ISO 180/1A | |
23℃ (73℉) | *** kJ/m² | ISO 180/1A | |
| Hardness | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Rockwell M | *** M | ISO 2039-2 | |
Rockwell R | *** R | ISO 2039-2 | |
Ball Indentation Hardness | *** Mpa | ISO 2039-1 | H 961/30 |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ISO 75-1/-2 | |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75-1/-2 | |
Vicat Softening Temperature(VST) | *** °C | ISO 306/B50 | 50°C/h, 50N |
Relative Temperature Index(RTI), Imp | |||
0.75/0.8mm | *** °C | UL 746B | |
1.5/1.6 mm | *** °C | UL 746B | |
3.0/3.2 mm | *** °C | UL 746B | |
Relative Temperature Index(RTI), Elec | |||
0.75/0.8mm | *** °C | UL 746B | |
1.5/1.6 mm | *** °C | UL 746B | |
3.0/3.2 mm | *** °C | UL 746B | |
Relative Temperature Index(RTI), Str | |||
0.75/0.8mm | *** °C | UL 746B | |
1.5/1.6 mm | *** °C | UL 746B | |
3.0/3.2 mm | *** °C | UL 746B | |
Coefficient of Linear Thermal Expansion | |||
Flow | *** E-6/K | ISO 11359-1/-2 | |
Across Flow | *** E-6/K | ISO 11359-1/-2 | |
Melt Temperature(Tm) | *** °C | ISO 11357-1/-3 | 10°C/min |
Thermal Diffusivity | *** m²/s | - | |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Flame Rating | |||
HB | *** mm | UL94 | |
HB | *** mm | UL94 | |
HB | *** mm | IEC 60695-11-10 | |
HB | *** mm | IEC 60695-11-10 | |
Glow Wire Flammability Index(GWFI) | |||
1mm | *** °C | IEC 60695-2-12 | |
2mm | *** °C | IEC 60695-2-12 | |
3mm | *** °C | IEC 60695-2-12 | |
FMVSS | *** - | FMVSS 302 | |
FMVSS | *** mm/min | FMVSS 302 | 1mm |
Burning Rate | *** mm/min | ISO 3795 | 1mm |
| Electrical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Volume Resistivity | *** Ohm-m | IEC 62631-3-1 | |
Surface Resistivity | > *** Ohm | IEC 62631-3-2 | |
Dielectric Constant(Permittivity) | |||
100Hz | *** - | IEC 62631-2-1 | |
1MHz | *** - | IEC 62631-2-1 | |
Dissipation Factor | |||
1MHz | *** E-4 | IEC 62631-2-1 | |
Comparative Tracking Index (CTI) | |||
- | *** V | IEC 60112 | |
Hot Wire Ignition(HWI) | *** sec | UL 746A | 0.75mm |
| Additional Information | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Fogging | |||
F-value (refraction) | *** % | ISO 6452 | |
G-value (condensate) | *** mg | ISO 6452 | |
Volatile Organic Compounds | < *** mg/kg | VDA 275 |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.