物性表(英文) 

POM

抗紫外线

耐候性

中粘度

均聚物

脱模剂

润滑剂

粒状

本色

注塑

N粘度-剪切速度 200|1/s|Pa s|Shear rate in 1/s|Viscosity in Pa s|100:538@200:471@500:351@1000:256@2000:173@5000:97@10000:61{n}215|1/s|Pa s|Shear rate in 1/s|Viscosity in Pa s|100:444@200:397@500:306@1000:229@2000:158@5000:90@10000:56{n}230|1/s|Pa s|Shear rate in 1/s|Viscosity in Pa s|100:370@200:336@500:268@1000:205@2000:145@5000:84@10000:53

剪切应力-剪切速率 200|1/s|Pa|Shear rate in 1/s|Shearstress in Pa|100:53800@200:94200@500:175500@1000:256000@2000:346000@5000:485000@10000:610000{n}215|1/s|Pa|Shear rate in 1/s|Shearstress in Pa|100:44400@200:79400@500:153000@1000:229000@2000:316000@5000:450000@10000:560000{n}230|1/s|Pa|Shear rate in 1/s|Shearstress in Pa|100:37000@200:67200@500:134000@1000:205000@2000:290000@5000:420000@10000:530000

动态剪切模量 (G 储能)-温度 G'|°C|MPa|Temperature in °C|G' in MPa|-50:1383.9@-40:1326.8@-30:1269.1@-20:1214.7@-10:1157.7@10:1042.6@20:983.4@30:919.5@40:851.8@50:770.6@60:670.7@70:568.9@80:488.4@90:421.7@100:361.6@110:307@120:255.4@130:209.4@140:169.8@150:136.1

应力-应变(Yield) -40|%|Mpa|Strain in %|Stress in MPa|0:0@1:35.1@2:61.2@3:77.5@4:87.3@5:92.5@6:95.40000000000001@7:97.7@8:98.3@9:98.90000000000001@10:99.09999999999999{n}-20|%|Mpa|Strain in %|Stress in MPa|0:0@2.6:66@3.9:75@5.2:79.5@6.5:81.3@7.8:82.3@9.1:83.09999999999999@10.4:83.5@11.7:83.8@13:84{n}0|%|Mpa|Strain in %|Stress in MPa|0:0@2.4:57.3@3.6:65@4.8:68.8@6:70.59999999999999@7.2:72@8.4:72.7@10.8:73.3@12:73.5{n}23|%|Mpa|Strain in %|Stress in MPa|0:0@2.5:47.2@3.7:56.1@4.9:61.1@6.2:63.8@7.4:65.5@8.6:66.40000000000001@9.800000000000001:67.09999999999999@12.3:67.5{n}40|%|Mpa|Strain in %|Stress in MPa|0:0@2.5:44@3.8:50@5:54@6.3:56@7.5:57@9:58@11.5:58.5{n}60|%|Mpa|Strain in %|Stress in MPa|0:0@1.2:18.5@2.3:29.5@3.5:36.2@4.6:41.2@5.8:44@6.9:45.8@8.1:46.5@11.4:47.4{n}80|%|Mpa|Strain in %|Stress in MPa|0:0@1.1:12.1@2.1:20.9@3.2:27.1@4.2:31.5@5.3:34.4@6.3:36.1@7.4:37.2@8.4:37.8@10.5:38.4{n}90|%|Mpa|Strain in %|Stress in MPa|0:0@1.2:11.4@2.4:18.9@3.6:24.1@4.8:28@6.1:30.3@7.3:31.4@8.5:32@9.699999999999999:32.2@12.1:32.5{n}100|%|Mpa|Strain in %|Stress in MPa|0:0@2.1:16.5@3.1:21.3@4.2:24.7@5.2:27.1@6.3:28.6@7.3:29.5@8.4:30@9.4:30.3@10.4:30.5{n}120|%|Mpa|Strain in %|Stress in MPa|0:0@1:7.1@2:12.3@3:16@4:18.3@5:20@6:21@7:21.7@8:22.1@9:22.3@10:22.4

正割模量-应变(Yield) -40|%|MPa|Strain in %|Secant modulus in MPa|1:3510@2:3060@3:2583.33@4:2182.5@5:1850@6:1590@7:1395.71@8:1228.75@9:1098.89@10:991{n}-20|%|MPa|Strain in %|Secant modulus in MPa|2.6:2538.46@3.9:1923.08@5.2:1528.85@6.5:1250.77@7.8:1055.13@9.1:913.187@10.4:802.885@11.7:716.239@13:646.154{n}0|%|MPa|Strain in %|Secant modulus in MPa|2.4:2387.5@3.6:1805.56@4.8:1433.33@6:1176.67@7.2:1000@8.4:865.476@10.8:678.704@12:612.5{n}23|%|MPa|Strain in %|Secant modulus in MPa|2.5:1888@3.7:1516.22@4.9:1246.94@6.2:1029.03@7.4:885.135@8.6:772.093@9.800000000000001:684.694@12.3:548.7809999999999{n}40|%|MPa|Strain in %|Secant modulus in MPa|2.5:1760@3.8:1315.79@5:1080@6.3:888.889@7.5:760@9:644.444@11.5:508.696{n}60|%|MPa|Strain in %|Secant modulus in MPa|1.2:1541.67@2.3:1282.61@3.5:1034.29@4.6:895.652@5.8:758.621@6.9:663.768@8.1:574.074@11.4:415.789{n}80|%|MPa|Strain in %|Secant modulus in MPa|1.1:1100@2.1:995.2380000000001@3.2:846.875@4.2:750@5.3:649.057@6.3:573.016@7.4:502.703@8.4:450@10.5:365.714{n}90|%|MPa|Strain in %|Secant modulus in MPa|1.2:950@2.4:787.5@3.6:669.444@4.8:583.333@6.1:496.721@7.3:430.137@8.5:376.471@9.699999999999999:331.959@12.1:268.595{n}100|%|MPa|Strain in %|Secant modulus in MPa|2.1:785.7140000000001@3.1:687.097@4.2:588.095@5.2:521.154@6.3:453.968@7.3:404.11@8.4:357.143@9.4:322.34@10.4:293.269{n}120|%|MPa|Strain in %|Secant modulus in MPa|1:710@2:615@3:533.333@4:457.5@5:400@6:350@7:310@8:276.25@9:247.778@10:224

应力-应变 (等时的) 23°C 1|%|MPa|Strain in %|Stress in MPa|0:0@0.15:4@0.26:6{n}10|%|MPa|Strain in %|Stress in MPa|0:0@0.17:4@0.27:6{n}100|%|MPa|Strain in %|Stress in MPa|0:0@0.19:4@0.3:6{n}1000|%|MPa|Strain in %|Stress in MPa|0:0@0.23:4@0.35:6{n}10000|%|MPa|Strain in %|Stress in MPa|0:0@0.32:4@0.51:6@2:18{n}100000|%|MPa|Strain in %|Stress in MPa|0:0@0.49:4@0.76:6

蠕变模量-时间 23°C 1|h|MPa|Time in h|Creep modulus in MPa|1:3121.95@10:2490.27@100:2214.53@1000:1763.09@10000:1317.26@100000:843.215{n}2|h|MPa|Time in h|Creep modulus in MPa|1:3018.87@10:2461.54@100:2191.78@1000:1758.24@10000:1303.24@100000:837.696{n}3|h|MPa|Time in h|Creep modulus in MPa|1:2861.4@10:2415.09@100:2154.88@1000:1750.23@10000:1280.51@100000:828.658{n}4|h|MPa|Time in h|Creep modulus in MPa|1:2666.67@10:2352.94@100:2105.26@1000:1739.13@10000:1250@100000:816.327{n}5|h|MPa|Time in h|Creep modulus in MPa|1:2465.33@10:2282.45@100:2048.66@1000:1726@10000:1213.83@100000:802.005{n}6|h|MPa|Time in h|Creep modulus in MPa|1:2307.69@10:2222.22@100:2000@1000:1714.29@10000:1176.47@100000:789.474

比容-温度(pvT) 0.1|°C|E-3 m³/kg|Spec. volume in °C|Temperature in E-3 m³/kg|20:0.705@40:0.711@60:0.718@80:0.727@100:0.741@120:0.764@140:0.8080000000000001@160:0.836@180:0.845@200:0.855@220:0.865{n}40|°C|E-3 m³/kg|Spec. volume in °C|Temperature in E-3 m³/kg|20:0.699@40:0.705@60:0.712@80:0.72@100:0.732@120:0.752@140:0.789@160:0.82@180:0.828@200:0.836@220:0.844{n}120|°C|E-3 m³/kg|Spec. volume in °C|Temperature in E-3 m³/kg|20:0.6889999999999999@40:0.694@60:0.7@80:0.707@100:0.717@120:0.732@140:0.759@160:0.796@180:0.802@200:0.8090000000000001@220:0.8149999999999999{n}200|°C|E-3 m³/kg|Spec. volume in °C|Temperature in E-3 m³/kg|20:0.679@40:0.6850000000000001@60:0.6899999999999999@80:0.697@100:0.705@120:0.717@140:0.737@160:0.775@180:0.783@200:0.788@220:0.793

拉伸模量-温度 |°C|MPa|Temperature in °C|Tensile modulus in MPa|-40:4361@-20:3572@0:3468@23:3242@40:2297@60:1770@80:1103@90:779@120:644