Delrin® RAFG100 NC010 is a high viscosity acetal homopolymer for use in easy-to-fill molds with reduced lifecycle greenhouse gas emissions and lower fossil resource use.
Delrin® RAFG100 NC010 provides a great combination of toughness and strength, and improved processing thermal stability and productivity for injection molding. It has been developed for applications in contact with food.
| 原厂资料 | 物性表(英文) | |||
| 树脂缩写 | POM | |||
| 产品特性 | 生物基食品接触级高粘度均聚物 | |||
| 颜色形状 | 粒状本色 | |||
| 成型方式 | 注塑挤出片材挤出型材挤出 | |||
| 曲线坐标点 | 正割模量-应变(Yield)应力-应变(Yield) | |||
| 生物基可再生 | 是 | |||
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.42 g/cm³ | ISO 1183 | |
熔体体积流动速率(MVR) | |||
190℃/2.16 kg | 1.9 cm³/10min | ISO 1133 | |
熔体质量流动速率(MFR) | |||
190℃/2.16 kg | 2.3 g/10min | ISO 1133 | |
收缩率 | |||
纵向(Flow) | 2 % | ISO 294-4, 2577 | |
横向(Across Flow) | 1.9 % | ISO 294-4, 2577 | |
吸水率 | 0.9 % | ISO 62 | 2mm |
吸湿率 | 0.2 % | ISO 62 | 2mm |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 71 Mpa | ISO 527-1/-2 | |
拉伸延伸率 | |||
屈服(yld) | 25 % | ISO 527-1/-2 | |
标称断裂伸长率 | 45 % | ISO 527-1/-2 | |
弯曲模量 | 2700 Mpa | ISO 178 | |
拉伸模量 | 3000 Mpa | ISO 527-1/-2 | |
拉伸蠕变模量 | |||
1h | 2900 Mpa | ISO 899-1 | |
1000h | 1600 Mpa | ISO 899-1 | |
泊松比 | 0.37 - | - | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-30℃ (-22℉) | 11 kJ/m² | ISO 179/1eA | |
23℃ (73℉) | 15 kJ/m² | ISO 179/1eA | |
简支梁无缺口(Charpy Unnotched) | |||
-30℃ (-22℉) | NB kJ/m² | ISO 179/1eU | |
23℃ (73℉) | NB kJ/m² | ISO 179/1eU | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 165 °C | ISO 75-1/-2 | |
1.8 Mpa (264 psi)（18.6kg/cm²） | 98 °C | ISO 75-1/-2 | |
相对温度指数(RTI) | |||
冲击Imp,0.75/0.8mm | 50 °C | UL 746B | |
冲击Imp,1.5/1.6 mm | 85 °C | UL 746B | |
冲击Imp,3.0/3.2 mm | 85 °C | UL 746B | |
冲击Imp,6.0mm | 85 °C | UL 746B | |
电气Elec,0.75/0.8mm | 50 °C | UL 746B | |
电气Elec,1.5/1.6 mm | 105 °C | UL 746B | |
电气Elec,3.0/3.2 mm | 105 °C | UL 746B | |
电气Elec,6.0mm | 105 °C | UL 746B | |
强度Str,0.75/0.8mm | 50 °C | UL 746B | |
强度Str,1.5/1.6 mm | 90 °C | UL 746B | |
强度Str,3.0/3.2 mm | 90 °C | UL 746B | |
强度Str,6.0mm | 90 °C | UL 746B | |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 110 E-6/K | ISO 11359-1/-2 | |
横向(Across Flow) | 110 E-6/K | ISO 11359-1/-2 | |
熔融温度(Tm) | 178 °C | ISO 11357-1/-3 | 10°C/min |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
HB | 0.75 mm | UL94 | |
HB | 1.5 mm | UL94 | |
HB | 0.75 mm | IEC 60695-11-10 | |
HB | 1.5 mm | IEC 60695-11-10 |