Delrin® RA100CPE is a high viscosity acetal homopolymer for use in easy-to-fill moulds with very low VOC emissions, reduced lifecycle greenhouse gas emissions and lower fossil resource use. Delrin® RA100CPE provides optimum mechanical performance with its excellent combination of toughness and strength with improved processing, thermal stability and productivity for injection moulding.
| 原厂资料 | 物性表(英文) | |||
| 树脂缩写 | POM | |||
| 产品特性 | 热稳定易成型短周期成型生物基低挥发VOC高粘度均聚物 | |||
| 颜色形状 | 粒状本色 | |||
| 成型方式 | 注塑挤出片材挤出 | |||
| 曲线坐标点 | N粘度-剪切速度剪切应力-剪切速率应力-应变正割模量-应变拉伸模量-温度应变-时间 (蠕变曲线 90°C) | |||
| 生物基可再生 | 是 | |||
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.42 g/cm³ | ISO 1183 | |
熔体体积流动速率(MVR) | |||
190℃/2.16 kg | 1.9 cm³/10min | ISO 1133 | |
熔体质量流动速率(MFR) | |||
190℃/2.16 kg | 2.3 g/10min | ISO 1133 | |
收缩率 | |||
纵向(Flow) | 2.2 % | ISO 294-4, 2577 | |
横向(Across Flow) | 1.9 % | ISO 294-4, 2577 | |
吸水率 | 1 % | ISO 62 | 2mm |
吸湿率 | 0.1 % | ISO 62 | 2mm |
熔体密度 | 1.18 g/cm³ | - | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 71 Mpa | ISO 527-1/-2 | |
拉伸延伸率 | |||
屈服(yld) | 28 % | ISO 527-1/-2 | |
标称断裂伸长率 | 45 % | ISO 527-1/-2 | |
弯曲强度 | |||
3.5%应变 | 76 Mpa | ISO 178 | |
弯曲模量 | 2800 Mpa | ISO 178 | |
拉伸模量 | 2900 Mpa | ISO 527-1/-2 | |
泊松比 | 0.37 - | - | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-30℃ (-22℉) | 13 kJ/m² | ISO 179/1eA | |
23℃ (73℉) | 16 kJ/m² | ISO 179/1eA | |
简支梁无缺口(Charpy Unnotched) | |||
-30℃ (-22℉) | 450 kJ/m² | ISO 179/1eU | |
23℃ (73℉) | NB kJ/m² | ISO 179/1eU | |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
洛氏硬度 M | 90 M | ISO 2039-2 | |
洛氏硬度R | 120 R | ISO 2039-2 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 160 °C | ISO 75-1/-2 | |
1.8 Mpa (264 psi)（18.6kg/cm²） | 95 °C | ISO 75-1/-2 | |
相对温度指数(RTI) | |||
冲击Imp,0.75/0.8mm | 50 °C | UL 746B | |
冲击Imp,1.5/1.6 mm | 85 °C | UL 746B | |
冲击Imp,3.0/3.2 mm | 90 °C | UL 746B | |
电气Elec,0.75/0.8mm | 50 °C | UL 746B | |
电气Elec,1.5/1.6 mm | 110 °C | UL 746B | |
电气Elec,3.0/3.2 mm | 110 °C | UL 746B | |
强度Str,0.75/0.8mm | 50 °C | UL 746B | |
强度Str,1.5/1.6 mm | 90 °C | UL 746B | |
强度Str,3.0/3.2 mm | 95 °C | UL 746B | |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 110 E-6/K | ISO 11359-1/-2 | |
纵向(Flow) | 95 E-6/K | ISO 11359-1/-2 | -40-23°C |
横向(Across Flow) | 100 E-6/K | ISO 11359-1/-2 | |
横向(Across Flow) | 100 E-6/K | ISO 11359-1/-2 | -40-23°C |
熔融温度(Tm) | 178 °C | ISO 11357-1/-3 | 10°C/min |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
HB | 0.8 mm | UL94 | |
HB | 1.5 mm | UL94 | |
HB | 0.8 mm | IEC 60695-11-10 | |
HB | 1.5 mm | IEC 60695-11-10 | |
FMVSS | B - | FMVSS 302 | |
FMVSS | 23 mm/min | FMVSS 302 | 1mm |
燃烧速率 | 23 mm/min | ISO 3795 | 1mm |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 1.0E+13 Ohm-m | IEC 62631-3-1 | |
表面电阻率 | 6.0E+14 Ohm | IEC 62631-3-2 | |
介电常数(DK) | |||
100Hz | 4.1 - | IEC 62631-2-1 | |
1MHz | 4 - | IEC 62631-2-1 | |
耗散因数(DF) | |||
100Hz | 25 E-4 | IEC 62631-2-1 | |
1MHz | 45 E-4 | IEC 62631-2-1 | |
相对漏电起痕指数(CTI ) | |||
- | 600 V | IEC 60112 | |
| 其他性能 | 值/单位 | 测试标准 | 测试条件 |
凝雾实验 | |||
F值（折射） | 81 % | ISO 6452 | |
G值（凝聚物） | 1 mg | ISO 6452 | |
VOC挥发 | 2 mg/kg | VDA 275 | |
VOC挥发 | 0.3 µgC/g | VDA 277 | |
VOC挥发 | 0.6 µg/g | VDA 278 |
此物性表中的信息由阿技材料库从该材料的生产商处获得。阿技材料库尽最大努力确保此数据的准确性。 但是阿技材料库对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。