Special PA 40% glass fibre reinforced, high flow injection moulding grade. Heat stabilized. Drinking water and food contact. Natural colour.
General purpose metal replacement product with good resistance to hydrolysis, enhanced mechanical properties after moisture pick-up. Specifically intended for use in applications in civil and industrial water management as well as appliances and consumer goods. Suitable for parts requiring high stiffness, good mechanical resistance along with high surface quality and superior gloss.
| Original Document | Technical Datasheet(English) | |||
| Resin ID | (PA66+PA)-GF40 | |||
| Availability | AsiaEuropeNorth AmericaMiddle EastLatin AmericaAfricaAustralia and New ZealandSouth & Central America | |||
| Features | High Stiffness/RigidityHeat StabilizedGood SurfaceHigh GlossFood ContactDrinking Water ContactHydrolysis ResistanceHigh FlowFilled & Reinforced | |||
| Additive | Release Agent | |||
| Applications | Metal replacement | |||
| Markets | Industrial ApplicationsConsumer ProductsDrinking & Waste Water Technology | |||
| Appearance | Pellets/GranulesNatural Color | |||
| Processing | Injection | |||
| Reinforced | 40% Glass Fiber | |||
| Physical | Dry/Cond.(Sign in to View) | Unit | Test Standard | Test Condition |
|---|---|---|---|---|
Density/Specific Gravity | ***/ *** | g/cm³ | ISO 1183 | |
Mold Shrinkage | ||||
Flow | ***/ * | % | ISO 294-4 | 290°C Melt Temp, 80°C Mold Temp, 60 MPa Cavity Press |
Across Flow | ***/ * | % | ISO 294-4 | 290°C Melt Temp, 80°C Mold Temp, 60 MPa Cavity Press |
| Mechanical | Dry/Cond.(Sign in to View) | Unit | Test Standard | Test Condition |
Tensile Modulus | ***/ *** | Mpa | ISO 527-2/1A | 1mm/min |
Tensile Strength | ||||
Break | ***/ *** | Mpa | ISO 527-2/1A | 5mm/min |
Tensile Elongation | ||||
Break | ***/ *** | % | ISO 527-2/1A | 5mm/min |
Flexural Modulus | ***/ *** | Mpa | ISO 178 | 2mm/min |
Flexural Strength | ||||
- | ***/ *** | Mpa | ISO 178 | 2mm/min |
| Impact | Dry/Cond.(Sign in to View) | Unit | Test Standard | Test Condition |
Charpy Notched Impact Strengh | ||||
23℃ (73℉) | ***/ * | kJ/m² | ISO 179/1eA | |
Charpy Unnotched Impact Strengh | ||||
23℃ (73℉) | ***/ * | kJ/m² | ISO 179/1eU | |
| Thermal | Dry/Cond.(Sign in to View) | Unit | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | ||||
1.8 Mpa (264 psi)（18.6kg/cm²） | ***/ * | °C | ISO 75/Af | |
Melt Temperature(Tm) | ***/ * | °C | ISO 11357-1/-3 | 10°C/min |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.