PA66 50% glass fibre reinforced injection moulding grade. Improved UV resistance. Black colour.
Suitable for parts requiring very high stiffness and high mechanical resistance, as in case of metal replacement applications, good heat ageing properties retention.
| Original Document | Technical Datasheet(English) | |||
| Resin ID | PA66-GF50 | |||
| Availability | AsiaEuropeNorth AmericaMiddle EastLatin AmericaAfricaAustralia and New ZealandSouth & Central America | |||
| Features | High Stiffness/RigidityHeat StabilizedGood Heat AgingUV StabiltiyFilled & Reinforced | |||
| Additive | Release Agent | |||
| Applications | Technical PartsMetal replacement | |||
| Markets | Automotive | |||
| Appearance | Pellets/GranulesBlack | |||
| Processing | Injection | |||
| Reinforced | 50% Glass Fiber | |||
| Physical | Dry/Cond.(Sign in to View) | Unit | Test Standard | Test Condition |
|---|---|---|---|---|
Density/Specific Gravity | ***/ *** | g/cm³ | ISO 1183 | |
Mold Shrinkage | ||||
Flow | ***/ * | % | ISO 294-4 | 300°C Melt Temp, 90°C Mold Temp, 60 MPa Cavity Press |
Across Flow | ***/ * | % | ISO 294-4 | 300°C Melt Temp, 90°C Mold Temp, 60 MPa Cavity Press |
Water Absorption | ***/ * | % | ISO 62 | immersion at 23°C, 2mm thk |
Moisture /Humidity Absorption | ***/ * | % | ISO 62 | 23°C/50%RH, 2mm thk |
| Mechanical | Dry/Cond.(Sign in to View) | Unit | Test Standard | Test Condition |
Tensile Modulus | ***/ *** | Mpa | ISO 527-2/1A | 1mm/min |
Tensile Strength | ||||
Break | ***/ *** | Mpa | ISO 527-2/1A | 5mm/min |
Tensile Elongation | ||||
Break | ***/ *** | % | ISO 527-2/1A | 5mm/min |
Flexural Modulus | ***/ *** | Mpa | ISO 178 | 2mm/min |
Flexural Strength | ||||
- | ***/ *** | Mpa | ISO 178 | 2mm/min |
| Impact | Dry/Cond.(Sign in to View) | Unit | Test Standard | Test Condition |
Charpy Notched Impact Strengh | ||||
23℃ (73℉) | ***/ *** | kJ/m² | ISO 179/1eA | |
Charpy Unnotched Impact Strengh | ||||
23℃ (73℉) | ***/ *** | kJ/m² | ISO 179/1eU | |
| Thermal | Dry/Cond.(Sign in to View) | Unit | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | ||||
1.8 Mpa (264 psi)（18.6kg/cm²） | ***/ * | °C | ISO 75-2/Af | |
Vicat Softening Temperature(VST) | ***/ * | °C | ISO 306/B50 | 50°C/h 50N |
Melt Temperature(Tm) | ***/ * | °C | ISO 11357-1/-3 | 10°C/min |
Thermal Conductivity | ***/ * | W/(m K) | - | 23°C, inplane |
| Flammability | Dry/Cond.(Sign in to View) | Unit | Test Standard | Test Condition |
Flame Rating | ||||
HB | ***/ * | mm | UL94 | |
Oxygen Index | ***/ * | % | ISO 4589-1/-2 | 23°C |
Glow Wire Flammability Index(GWFI) | ||||
2mm | ***/ * | °C | IEC 60695-2-12 | |
Burning Rate | / * | mm/min | ISO 3795 | 3mm |
| Electrical | Dry/Cond.(Sign in to View) | Unit | Test Standard | Test Condition |
Volume Resistivity | ***/ *** | Ohm-m | IEC 62631-3-1 | 500V |
Surface Resistivity | ***/ *** | Ohm | IEC 62631-3-2 | 500V |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.