Heat stabilized, partially aromatic polyphthalamide for injection molding with strong mechanical properties especially at elevated temperatures and good chemical resistance for highly stressed parts. The product can be characterized as compound with high strength and stiffness. It features a high melting point (310°C) and good heat resistance.
Markets & applications
Automotive: sensors, e-mobility
E&E: Connectors Consumer goods
| 原厂资料 | 物性表(英文) | |||
| 树脂缩写 | PA6T/66-GF30 | |||
| 产品特性 | 高刚性耐热热稳定耐化学性填充增强 | |||
| 应用产品 | 电动汽车汽车连接器连接器高应力部件传感器 | |||
| 成型方式 | 注塑 | |||
| 增强填充 | 30% 玻纤 | |||
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.39 g/cm³ | ISO 1183 | |
熔体体积流动速率(MVR) | |||
320°C/5.0 kg | 5 cm³/10 min | ISO 1133 | |
收缩率 | |||
纵向(Flow) | 0.5 % | ISO 294-4 | |
横向(Across Flow) | 1.1 % | ISO 294-4 | |
吸水率 | 4.2 % | ISO 62 | equilibrium in water at 23°C |
吸湿率 | 1.32 % | ISO 62 | equilibrium 23°C/50% r.h. |
粘度 | 130 cm³/g | ISO 307, 1157, 1628 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 160 Mpa | ISO 527-1/-2 | Cond. |
断裂(brk) | 190 Mpa | ISO 527-1/-2 | Dry |
拉伸延伸率 | |||
断裂(brk) | 3 % | ISO 527-1/-2 | Cond. |
断裂(brk) | 2.8 % | ISO 527-1/-2 | Dry |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 280 °C | ISO 75-1/-2 | |
1.8 Mpa (264 psi)（18.6kg/cm²） | 280 °C | ISO 75-1/-2 | |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 22 E-6/K | ISO 11359-1/-2 | 23℃-55℃ |
横向(Across Flow) | 72 E-6/K | ISO 11359-1/-2 | 23℃-55℃ |
熔融温度(Tm) | 310 °C | ISO 11357-1/-3 |
此物性表中的信息由阿技材料库从该材料的生产商处获得。阿技材料库尽最大努力确保此数据的准确性。 但是阿技材料库对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。