Ultramid A3XG3 BK20562 is a 15% glass fiber reinforced injection molding PA66 grade with improved flame retardance and enhanced long-term heat stability. The grade is based on red phosphorous and exhibits exceptional mechanical properties and outstanding surface finish. Flame performance has been determined to be V0 at 0.8mm per the UL94 method.
| 原厂资料 | ||||
| 产品特性 | 热稳定阻燃含磷良好表面填充增强 | |||
| 添加助剂 | 阻燃剂 | |||
| 颜色形状 | 粒状黑色 | |||
| 成型方式 | 注塑 | |||
| 汽车材料 | 通用(GM) GMW16428P | |||
| 增强填充 | 15% 玻纤 | |||
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.34 g/cm³ | ISO 1183 | |
收缩率 | |||
纵向(Flow) | 0.5 % | ISO 294-4 | |
横向(Across Flow) | 1.1 % | ISO 294-4 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 72 Mpa | ISO 527-1/-2 | cond |
断裂(brk) | 120 Mpa | ISO 527-1/-2 | dry |
拉伸延伸率 | |||
断裂(brk) | 5.6 % | ISO 527-1/-2 | cond |
断裂(brk) | 2.8 % | ISO 527-1/-2 | dry |
拉伸模量 | 4450 Mpa | ISO 527-1/-2 | cond |
拉伸模量 | 6740 Mpa | ISO 527-1/-2 | dry |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
23℃ (73℉) | 5.6 kJ/m² | ISO 179/1eA | cond |
23℃ (73℉) | 4.8 kJ/m² | ISO 179/1eA | dry |
简支梁无缺口(Charpy Unnotched) | |||
23℃ (73℉) | 49 kJ/m² | ISO 179/1eU | cond |
23℃ (73℉) | 45 kJ/m² | ISO 179/1eU | dry |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 250 °C | ISO 75-1/-2 | |
1.8 Mpa (264 psi)（18.6kg/cm²） | 222 °C | ISO 75-1/-2 | |
熔融温度(Tm) | 260 °C | ISO 11357-1/-3 |
此物性表中的信息由阿技材料库从该材料的生产商处获得。阿技材料库尽最大努力确保此数据的准确性。 但是阿技材料库对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。