Ultramid TG3S BK-104 is a 15% glass reinforced, heat stabilized, impact modified PA6 injection molding compound developed for applications requiring improved toughness in combination with a balance of strength, stiffness, excellent moldability and surface aesthetics.
Applications
It is generally recommended for application such as window hardware, wheel chairs wheels, bicycle wheels, power tool housings, hose clamps, clips and fasteners.
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 增韧/冲击改性热稳定良好表面填充增强 | |||
| 颜色形状 | 粒状黑色 | |||
| 成型方式 | 注塑 | |||
| 汽车材料 | 福特(FORD) WSK-M4D665-A2斯泰兰蒂斯(Stellantis) MS-DB-41 | |||
| 增强填充 | 15% 玻纤 | |||
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.21 g/cm³ | ISO 1183 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 90 Mpa | ISO 527 | |
拉伸延伸率 | |||
断裂(brk) | 3.5 % | ISO 527 | |
弯曲模量 | 4390 Mpa | ISO 178 | |
拉伸模量 | 4600 Mpa | ISO 527 | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
23℃ (73℉) | 13 kJ/m² | ISO 179 | |
悬臂梁缺口(Izod Notched) | |||
-40℃ (-40℉) | 5.4 kJ/m² | ISO 180 | |
23℃ (73℉) | 17 kJ/m² | ISO 180 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 211 °C | ISO 75/B | |
1.8 Mpa (264 psi)（18.6kg/cm²） | 180 °C | ISO 75/A | |
相对温度指数(RTI) | |||
冲击Imp,- | 65 °C | UL 746B | |
电气Elec,- | 65 °C | UL 746B | |
强度Str,- | 65 °C | UL 746B | |
熔融温度(Tm) | 220 °C | ISO 3146 | |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
HB | 1.5 mm | UL94 |
此物性表中的信息由阿技材料库从该材料的生产商处获得。阿技材料库尽最大努力确保此数据的准确性。 但是阿技材料库对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。