Plexiglas® V825 is a thermoplastic acrylic resin formulated for injection molding and extrusion applications. It is characterized by its high heat resistance and high melt flow. Plexiglas® V825 has excellent weatherability and optical properties allowing it to excel in applications requiring outdoor stability, high quality surface appearance and/or precision optics. Plexiglas® V825 is easy to process due to its exceptional thermal stability, extrusion melt strength, and excellent tool surface reproduction and release properties. Moldflow simulation data is available. It has excellent resistance to many chemicals including solutions of inorganic acids, alkalis and aliphatic hydrocarbons such as heptane. Additionally, it is virtually unaffected by a wide range of commercial products including many beverages, foodstuffs, detergent solutions and cleaners.
| 原厂资料 | 物性表(英文) | |||
| 供应市场 | 北美 | |||
| 产品特性 | 耐热良好表面耐刮擦抗紫外线耐候性耐化学性耐酸耐碱耐洗涤剂耐碳氢化合物(烃)高流动 | |||
| 应用产品 | 汽车零部件 | |||
| 颜色形状 | 粒状透明 | |||
| 成型方式 | 注塑挤出 | |||
| 汽车材料 | 福特(FORD) WSS-M4D776-B1汽车工程师协会(SAE) SAE J576福特(FORD) WSS-M4D776-B2通用(GM) GMW16335P-PMMA-T2HF福特(FORD) ESF-M4D9-A福特(FORD) WSK-M4D776-A1通用(GM) GMP.PMMA.007通用(GM) GMP.PMMA.012现代-起亚(Hyundai-KIA) MS235-01 Type A斯泰兰蒂斯(Stellantis) MS-DB-14斯泰兰蒂斯(Stellantis) MS-DB-14 CPN2969斯泰兰蒂斯(Stellantis) MS-DB-75 CPN4231斯泰兰蒂斯(Stellantis) MS-DB-75 CPN4232 | |||
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
UL 防火等级 | |||
HB | - mm | UL94 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 105 °C | ASTM D648 | |
0.45 Mpa (66 psi)（4.6kg/cm²） | 98 °C | ISO 75-2/B | Annealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 90 °C | ASTM D648 | Annealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 93 °C | ISO 75-2/A | Annealed |
维卡软化温度(Vicat) | 108 °C | ASTM D1525 | Rate A (50°C/h), Loading 1 (10 N) |
维卡软化温度(Vicat) | 97.2 °C | ASTM D1525 | Rate A (50°C/h), Loading 2 (50 N) |
维卡软化温度(Vicat) | 103 °C | ISO 306/B50 | |
维卡软化温度(Vicat) | 108 °C | ISO 306/A50 | |
导热系数 | 0.19 W/(m K) | ASTM C 177 | |
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
密度 | 1.17 g/cm³ | ISO 1183 | |
密度 | 1.17 g/cm³ | ASTM D792 | |
熔体体积流动速率(MVR) | |||
230℃/3.8 kg | 2.1 cm³/10 min | ISO 1133 | |
熔体质量流动速率(MFR) | |||
230°C/3.8 kg | 1.8 g/10 min | ASTM D 1238 | |
230°C/3.8 kg | 2 g/10 min | ISO 1133 | |
收缩率 | |||
纵向(Flow) | 0.3~0.6 % | ASTM D 955 | |
- | 0.3~0.6 % | ISO 294-4 | |
吸水率 | 0.3 % | ASTM D570 | 24 hr |
吸水率 | 0.3 % | ISO 62 | 24 hr, 23°C |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 60 Mpa | ISO 527-2/1A/5 | |
断裂(brk) | 55.2 Mpa | ASTM D638 | |
断裂(brk) | 50 Mpa | ISO 527-2/1A/5 | |
拉伸延伸率 | |||
屈服(yld) | 5 % | ISO 527-2/1A/5 | |
断裂(brk) | 35 % | ASTM D638 | |
断裂(brk) | 35 % | ISO 527-2/1A/5 | |
弯曲强度 | |||
断裂(brk) | 86.9 Mpa | ASTM D790 | |
- | 70 Mpa | ISO 178 | |
弯曲模量 | 2410 Mpa | ASTM D790 | |
弯曲模量 | 2400 Mpa | ISO 178 | |
拉伸模量 | 2410 Mpa | ASTM D638 | |
拉伸模量 | 2500 Mpa | ISO 527-1/1A/1 | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
- | 4 kJ/m² | ISO 179/1eA | |
简支梁无缺口(Charpy Unnotched) | |||
- | 40 kJ/m² | ISO 179/1eU | |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 32 J/m | ASTM D256 | |
- | 5 kJ/m² | ISO 180/A | |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
洛氏硬度 M | 68 M | ISO 2039-2 | |
洛氏硬度 M | 68 M | ASTM D 785 | |
| 光学性能 | 值/单位 | 测试标准 | 测试条件 |
透光率 | 92 % | ASTM D1003 | 3175 µm |
雾度 | 2 % | ASTM D1003 | 3175 µm |
折射率 | 1.49 - | ASTM D542 | |
折射率 | 1.49 - | ISO 489 |