Plexiglas® V052i is a lightly impact modified thermoplastic acrylic resin formulated for injection molding. It is characterized by its chemical and heat resistance as well a good melt flow and excellent mold release properties. It is a tougher resin than Plexiglas® V052 allowing improved fabrication. It offers an excellent balance between melt flow and increased resistance to breakage, while providing weatherability superior to that provided by other high-impact plastics. Moldflow simulation data is available.
| 原厂资料 | 物性表(英文) | |||
| 供应市场 | 北美 | |||
| 产品特性 | 增韧/冲击改性耐热易脱模抗紫外线耐候性耐化学性 | |||
| 添加助剂 | 抗冲击剂 | |||
| 颜色形状 | 粒状透明 | |||
| 汽车材料 | 福特(FORD) WSS-M4D776-B1汽车工程师协会(SAE) SAE J576福特(FORD) WSS-M4D776-B5福特(FORD) ESF-M4D9-A通用(GM) GMP.PMMA.006通用(GM) GMW16335P-PMMA-T3斯泰兰蒂斯(Stellantis) MS-DB-75 CPN4237斯泰兰蒂斯(Stellantis) MS-DB-16 CPN4083 | |||
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.18 g/cm³ | ISO 1183 | |
密度 | 1.18 g/cm³ | ASTM D792 | |
熔体体积流动速率(MVR) | |||
230℃/3.8 kg | 2.9 cm³/10 min | ISO 1133 | |
熔体质量流动速率(MFR) | |||
230°C/3.8 kg | 3 g/10 min | ASTM D 1238 | |
230°C/3.8 kg | 3.1 g/10 min | ISO 1133 | |
收缩率 | |||
纵向(Flow) | 0.2~0.6 % | ASTM D 955 | |
- | 0.2~0.6 % | ISO 294-4 | |
吸水率 | 0.4 % | ASTM D570 | 24 hr |
吸水率 | 0.4 % | ISO 62 | 24 hr, 23°C |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 70 Mpa | ISO 527-2/1A/5 | |
断裂(brk) | 63.4 Mpa | ASTM D638 | |
断裂(brk) | 60 Mpa | ISO 527-2/1A/5 | |
拉伸延伸率 | |||
屈服(yld) | 5 % | ISO 527-2/1A/5 | |
断裂(brk) | 22 % | ASTM D638 | |
断裂(brk) | 20 % | ISO 527-2/1A/5 | |
弯曲强度 | |||
断裂(brk) | 96.5 Mpa | ASTM D790 | |
- | 85 Mpa | ISO 178 | |
弯曲模量 | 2900 Mpa | ASTM D790 | |
弯曲模量 | 2700 Mpa | ISO 178 | |
拉伸模量 | 2830 Mpa | ASTM D638 | |
拉伸模量 | 3000 Mpa | ISO 527-1/1A/1 | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
- | 2 kJ/m² | ISO 179/1eA | |
简支梁无缺口(Charpy Unnotched) | |||
- | 20 kJ/m² | ISO 179/1eU | |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 21 J/m | ASTM D256 | |
- | 3 kJ/m² | ISO 180/A | |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
洛氏硬度 M | 84 M | ISO 2039-2 | |
洛氏硬度 M | 84 M | ASTM D 785 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 103 °C | ASTM D648 | Annealed |
0.45 Mpa (66 psi)（4.6kg/cm²） | 95 °C | ISO 75-2/B | Annealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 97.2 °C | ASTM D648 | Annealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 91 °C | ISO 75-2/A | Annealed |
维卡软化温度(Vicat) | 110 °C | ASTM D1525 | Rate A (50°C/h), Loading 1 (10 N) |
维卡软化温度(Vicat) | 102 °C | ASTM D1525 | Rate A (50°C/h), Loading 2 (50 N) |
维卡软化温度(Vicat) | 102 °C | ISO 306/B50 | |
维卡软化温度(Vicat) | 108 °C | ISO 306/A50 | |
导热系数 | 0.19 W/(m K) | ASTM C 177 | |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
HB | - mm | UL94 | |
| 光学性能 | 值/单位 | 测试标准 | 测试条件 |
透光率 | 91 % | ASTM D1003 | 3175 µm |
雾度 | 2 % | ASTM D1003 | 3175 µm |
折射率 | 1.49 - | ASTM D542 | |
折射率 | 1.49 - | ISO 489 |
此物性表中的信息由阿技材料库从该材料的生产商处获得。阿技材料库尽最大努力确保此数据的准确性。 但是阿技材料库对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。