PA66 injection moulding grade. Internally lubricated. Fast cycling. Natural colour.
General purpose grade, suitable for parts requiring high productivity like fasteners, connectors, cable ties.
| Original Document | Technical Datasheet(English) | |||
| Resin ID | PA66 | |||
| Availability | AsiaEuropeNorth AmericaMiddle EastLatin AmericaAfricaAustralia and New ZealandSouth & Central America | |||
| Features | Self LubricatingFast Cycle Time | |||
| Additive | Release AgentLubricant | |||
| Applications | FastenersConnectorsTies | |||
| Markets | Industrial ApplicationsConsumer ProductsRail Technology and VehiclesTransportation | |||
| Appearance | Pellets/GranulesNatural Color | |||
| Processing | Injection | |||
| Diagrams | Stress-strainStress-strain (Cond.)Secant modulus-strainSecant modulus-strain (Cond.)Coefficient of Linear Thermal Expansion(CTE)-TemperatureViscosity-shear rateShearstress-shear rate | |||
| Physical | Dry/Cond.(Sign in to View) | Unit | Test Standard | Test Condition |
|---|---|---|---|---|
Density/Specific Gravity | ***/ *** | g/cm³ | ISO 1183 | |
Mold Shrinkage | ||||
Flow | ***/ * | % | ISO 294-4 | 290°C Melt Temp, 70°C Mold Temp, 60 MPa Cavity Press |
Across Flow | ***/ * | % | ISO 294-4 | 290°C Melt Temp, 70°C Mold Temp, 60 MPa Cavity Press |
Water Absorption | ***/ * | % | ISO 62 | immersion at 23°C, 2mm thk |
Moisture /Humidity Absorption | ***/ * | % | ISO 62 | 23°C/50%RH, 2mm thk |
Viscosity | ***/ * | cm³/g | ISO 307 | Sulfuric Acid |
| Mechanical | Dry/Cond.(Sign in to View) | Unit | Test Standard | Test Condition |
Tensile Modulus | ***/ *** | Mpa | ISO 527-2/1A | 1mm/min |
Tensile Strength | ||||
Yield | ***/ *** | Mpa | ISO 527-2/1A | 50mm/min |
Tensile Elongation | ||||
Yield | ***/ *** | % | ISO 527-2/1A | 50mm/min |
Nominal Tensile Strain at Break | ***/> *** | % | ISO 527-2/1A | 50mm/min |
Flexural Modulus | ***/ *** | Mpa | ISO 178 | 2mm/min |
Flexural Strength | ||||
- | ***/ *** | Mpa | ISO 178 | 2mm/min |
| Impact | Dry/Cond.(Sign in to View) | Unit | Test Standard | Test Condition |
Charpy Notched Impact Strengh | ||||
-30℃ (-22℉) | ***/ *** | kJ/m² | ISO 179/1eA | |
23℃ (73℉) | ***/ *** | kJ/m² | ISO 179/1eA | |
Charpy Unnotched Impact Strengh | ||||
23℃ (73℉) | ***/ *** | kJ/m² | ISO 179/1eU | |
| Thermal | Dry/Cond.(Sign in to View) | Unit | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | ||||
0.45 Mpa (66 psi)（4.6kg/cm²） | ***/ * | °C | ISO 75/Bf | |
1.8 Mpa (264 psi)（18.6kg/cm²） | ***/ * | °C | ISO 75/Af | |
Vicat Softening Temperature(VST) | ***/ * | °C | ISO 306/B50 | 50°C/h 50N |
Coefficient of Linear Thermal Expansion | ||||
Flow | ***/ * | E-6/K | ISO 11359-1/-2 | 23°C-55°C |
Across Flow | ***/ * | E-6/K | ISO 11359-1/-2 | 23°C-55°C |
Melt Temperature(Tm) | ***/ * | °C | ISO 11357-1/-3 | 10°C/min |
| Flammability | Dry/Cond.(Sign in to View) | Unit | Test Standard | Test Condition |
Flame Rating | ||||
V-2 | ***/ * | mm | UL94 | |
V-2 | ***/ * | mm | UL94 | |
Glow Wire Flammability Index(GWFI) | ||||
0.75mm | ***/ * | °C | IEC 60695-2-12 | |
1mm | ***/ * | °C | IEC 60695-2-12 | |
2mm | ***/ * | °C | IEC 60695-2-12 | |
Burning Rate | / * | mm/min | ISO 3795 | 3mm |
| Electrical | Dry/Cond.(Sign in to View) | Unit | Test Standard | Test Condition |
Volume Resistivity | ***/ *** | Ohm-m | IEC 62631-3-1 | 500V |
Surface Resistivity | ***/ *** | Ohm | IEC 62631-3-2 | 500V |
Comparative Tracking Index (CTI) | ||||
Solution A | ***/ *** | V | IEC 60112 |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.