PA66 injection moulding grade. Toughened. Natural colour.
Suitable for parts requiring good impact strength.
| Original Document | Technical Datasheet(English) | |||
| Resin ID | PA66-HI | |||
| Availability | AsiaEuropeNorth AmericaMiddle EastLatin AmericaAfricaAustralia and New ZealandSouth & Central America | |||
| Features | High ImpactToughened/Impact Modified | |||
| Additive | Release Agent | |||
| Markets | Industrial ApplicationsConsumer ProductsAutomotiveTransportation | |||
| Appearance | Pellets/GranulesNatural Color | |||
| Processing | Injection | |||
| Diagrams | Viscosity-shear rate 275|1/s|Pa s|Shear rate in 1/s|Viscosity in Pa s|27.49:535.798@137.43:351.1@549.72:204@824.59:175.3@2748.62:103.1@8245.870000000001:57.4{n}285|1/s|Pa s|Shear rate in 1/s|Viscosity in Pa s|27.49:429.302@137.43:233.7@549.72:147.5@824.59:127.7@2748.62:80.8999@8245.870000000001:46.3{n}295|1/s|Pa s|Shear rate in 1/s|Viscosity in Pa s|27.49:322.7@137.43:178.2@549.72:113.9@824.59:100.2@2748.62:64.5@8245.870000000001:38.3Shearstress-shear rate 275|1/s|Pa|Shear rate in 1/s|Shearstress in Pa|27.49:14729.1@137.43:48251.7@549.72:112143@824.59:144551@2748.62:283383@8245.870000000001:473313{n}285|1/s|Pa|Shear rate in 1/s|Shearstress in Pa|27.49:11801.5@137.43:32117.4@549.72:81083.7@824.59:105300@2748.62:222363@8245.870000000001:381784{n}295|1/s|Pa|Shear rate in 1/s|Shearstress in Pa|27.49:8871.02@137.43:24490@549.72:62613.1@824.59:82623.89999999999@2748.62:177286@8245.870000000001:315817Stress-strain -20|%|Mpa|Strain in %|Stress in MPa|0:0@0.016:1.07369@0.0303:1.85215@0.0743:3.40228@0.116:4.69097@1.14:29.5@2.26:50.4@3.44:67.2@5.00888:73.8557@5.69671:74.49290000000001@6.26567:74.6942{n}0|%|Mpa|Strain in %|Stress in MPa|0:0@0.0234:0.89246@0.0448:1.50987@0.0848:2.62388@0.1257:3.69106@0.699:15.8049@2.23012:47.6081@3.01244:58.5546@3.85064:64.3259@4.45008:65.66800000000001@4.93268:66.0372{n}23|%|Mpa|Strain in %|Stress in MPa|0:0@0.016:0.51672@0.038:1.1072@0.098:2.27493@0.157:3.38904@0.83:15.9116@2.16:40.6425@2.91084:48.9@3.72872:52.6@4.22656:54.3@4.66344:54.7{n}50|%|Mpa|Strain in %|Stress in MPa|0:0@0.254:3.6@0.509:7.2@1.317:17.09@2.148:27.25@3.046:33.68@4.129:36.72@5.475:38.07@6.586:38.77@7.697:39.4@8.808999999999999:40.01@9.92:40.43@11.124:40.71{n}80|%|Mpa|Strain in %|Stress in MPa|0:0@3.059:11.34@6.494:18.33@10.105:22.83@13.716:25.73@17.327:27.65@20.939:28.93@24.55:29.77@28.161:30.32@31.773:30.7@35.384:30.95@38.995:31.14@42.606:31.26{n}110|%|Mpa|Strain in %|Stress in MPa|0:0@2.03:7.35@4.04:13.05@7.038:17.21@10.649:19.92@14.261:21.72@17.872:22.99@21.483:23.91@25.094:24.59@28.705:25.1@32.317:25.48@35.928:25.76@39.632:25.99{n}170|%|Mpa|Strain in %|Stress in MPa|0:0@1.325:3.66@2.617:7.07@3.887:9.460000000000001@5.584:11.39@7.806:12.7@10.121:13.81@12.436:14.56@14.436:15.08@16.973:15.5@19.195:15.81@21.511:16.06@23.825:16.27Stress-strain (Cond.) 23|%|Mpa|Strain in %|Stress in MPa|0:0@0.073:0.64@0.126:1.1@0.18:1.56@0.232:2@1.126:9.49@4.009:21.72@7.64:27.29@11.343:30.46@15.14:32.47@18.844:33.64@22.547:34.21@26.344:34.5{n}50|%|Mpa|Strain in %|Stress in MPa|0:0@1.842:8.119999999999999@11.393:22.45@21.579:26.58@31.764:27.89@41.949:28.27@49.5:28.95Secant modulus-strain -20|%|MPa|Strain in %|Secant modulus in MPa|0.016:6710.56@0.0303:6112.71@0.0743:4579.11@0.116:4043.94@1.14:2587.72@2.26:2230.09@3.44:1953.49@5.00888:1474.5@5.69671:1307.65@6.26567:1192.12{n}0|%|MPa|Strain in %|Secant modulus in MPa|0.0234:3813.92@0.0448:3370.25@0.0848:3094.2@0.1257:2936.4@0.699:2261.07@2.23012:2134.78@3.01244:1943.76@3.85064:1670.52@4.45008:1475.66@4.93268:1338.77{n}23|%|MPa|Strain in %|Secant modulus in MPa|0.016:3229.52@0.038:2913.68@0.098:2321.36@0.157:2158.62@0.83:1917.06@2.16:1881.6@2.91084:1679.93@3.72872:1410.67@4.22656:1284.73@4.66344:1172.95{n}50|%|MPa|Strain in %|Secant modulus in MPa|0.254:1417.32@0.509:1414.54@1.317:1297.65@2.148:1268.62@3.046:1105.71@4.129:889.319@5.475:695.342@6.586:588.673@7.697:511.888@8.808999999999999:454.195@9.92:407.56@11.124:365.965{n}80|%|MPa|Strain in %|Secant modulus in MPa|3.059:370.709@6.494:282.261@10.105:225.928@13.716:187.591@17.327:159.578@20.939:138.163@24.55:121.263@28.161:107.667@31.773:96.6229@35.384:87.4689@38.995:79.85639999999999@42.606:73.3699{n}110|%|MPa|Strain in %|Secant modulus in MPa|2.03:362.069@4.04:323.02@7.038:244.53@10.649:187.06@14.261:152.303@17.872:128.637@21.483:111.297@25.094:97.99160000000001@28.705:87.44119999999999@32.317:78.8439@35.928:71.699@39.632:65.5783{n}170|%|MPa|Strain in %|Secant modulus in MPa|1.325:276.226@2.617:270.157@3.887:243.375@5.584:203.976@7.806:162.695@10.121:136.449@12.436:117.079@14.436:104.461@16.973:91.3215@19.195:82.3652@21.511:74.65949999999999@23.825:68.28959999999999Secant modulus-strain (Cond.) 23|%|MPa|Strain in %|Secant modulus in MPa|0.073:876.712@0.126:873.016@0.18:866.667@0.232:862.069@1.126:842.806@4.009:541.7809999999999@7.64:357.199@11.343:268.536@15.14:214.465@18.844:178.518@22.547:151.728@26.344:130.96{n}50|%|MPa|Strain in %|Secant modulus in MPa|1.842:440.825@11.393:197.051@21.579:123.175@31.764:87.8038@41.949:67.3914@49.5:58.4848 | |||
| Physical | Dry/Cond.(Sign in to View) | Unit | Test Standard | Test Condition |
|---|---|---|---|---|
Density/Specific Gravity | ***/ *** | g/cm³ | ISO 1183 | |
Mold Shrinkage | ||||
Flow | ***/ * | % | ISO 294-4 | 290°C Melt Temp, 70°C Mold Temp, 60 MPa Cavity Press |
Across Flow | ***/ * | % | ISO 294-4 | 290°C Melt Temp, 70°C Mold Temp, 60 MPa Cavity Press |
Water Absorption | ***/ * | % | ISO 62 | immersion at 23°C, 2mm thk |
Moisture /Humidity Absorption | ***/ * | % | ISO 62 | 23°C/50%RH, 2mm thk |
| Mechanical | Dry/Cond.(Sign in to View) | Unit | Test Standard | Test Condition |
Tensile Modulus | ***/ *** | Mpa | ISO 527-2/1A | 1mm/min |
Tensile Strength | ||||
Yield | ***/ *** | Mpa | ISO 527-2/1A | 50mm/min |
Tensile Elongation | ||||
Yield | ***/ *** | % | ISO 527-2/1A | 50mm/min |
Nominal Tensile Strain at Break | ***/< *** | % | ISO 527-2/1A | 50mm/min |
Flexural Modulus | ***/ *** | Mpa | ISO 178 | 2mm/min |
Flexural Strength | ||||
- | ***/ *** | Mpa | ISO 178 | 2mm/min |
| Impact | Dry/Cond.(Sign in to View) | Unit | Test Standard | Test Condition |
Charpy Notched Impact Strengh | ||||
-30℃ (-22℉) | ***/ *** | kJ/m² | ISO 179/1eA | |
23℃ (73℉) | ***/ *** | kJ/m² | ISO 179/1eA | |
Charpy Unnotched Impact Strengh | ||||
23℃ (73℉) | ***/ *** | kJ/m² | ISO 179/1eU | |
| Thermal | Dry/Cond.(Sign in to View) | Unit | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | ||||
0.45 Mpa (66 psi)（4.6kg/cm²） | ***/ * | °C | ISO 75/Bf | |
1.8 Mpa (264 psi)（18.6kg/cm²） | ***/ * | °C | ISO 75/Af | |
Vicat Softening Temperature(VST) | ***/ * | °C | ISO 306/B50 | 50°C/h 50N |
Melt Temperature(Tm) | ***/ * | °C | ISO 11357-1/-3 | 10°C/min |
| Flammability | Dry/Cond.(Sign in to View) | Unit | Test Standard | Test Condition |
Flame Rating | ||||
HB | ***/ * | mm | UL94 | |
Glow Wire Flammability Index(GWFI) | ||||
1mm | ***/ * | °C | IEC 60695-2-12 | |
Burning Rate | < ***/ * | mm/min | ISO 3795 | 3mm |
| Electrical | Dry/Cond.(Sign in to View) | Unit | Test Standard | Test Condition |
Volume Resistivity | ***/ *** | Ohm-m | IEC 62631-3-1 | 500V |
Surface Resistivity | ***/ *** | Ohm | IEC 62631-3-2 | 500V |
Comparative Tracking Index (CTI) | ||||
Solution A | ***/ *** | V | IEC 60112 |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.