PPA flame retardant injection moulding grade, 30% glass fibre reinforced. Halogen and red phosphorus free. High melting point. Natural colour.
Suitable for parts requiring fire retardancy along with high stiffness and good mechanical resistance. Suitable for Lead Free Soldering application. Rated V0 according to UL94.
| Original Document | Technical Datasheet(English) | |||
| Resin ID | PA6T/66-GF30 FR(40) | |||
| Availability | AsiaEuropeNorth AmericaMiddle EastLatin AmericaAfricaAustralia and New ZealandSouth & Central America | |||
| Additive | Flame RetardantRelease Agent | |||
| Applications | Lead Free Soldering application | |||
| Markets | AutomotiveElectrical / Electronics | |||
| Appearance | Pellets/GranulesNatural Color | |||
| Processing | Injection | |||
| Diagrams | Stress-strainSecant modulus-strainTensile modulus-temperatureViscosity-shear rateShearstress-shear rate | |||
| Reinforced | 30% Glass Fiber | |||
| Physical | Dry/Cond.(Sign in to View) | Unit | Test Standard | Test Condition |
|---|---|---|---|---|
Density/Specific Gravity | ***/ *** | g/cm³ | ISO 1183 | |
Mold Shrinkage | ||||
Flow | ***/ * | % | ISO 294-4 | 280°C Melt Temp, 70°C Mold Temp, 60 MPa Cavity Press |
Across Flow | ***/ * | % | ISO 294-4 | 280°C Melt Temp, 70°C Mold Temp, 60 MPa Cavity Press |
Water Absorption | ***/ * | % | ISO 62 | 24h immersion at 23°C, 2mm thk |
Moisture /Humidity Absorption | ***/ * | % | ISO 62 | 23°C/50%RH, 2mm thk |
| Mechanical | Dry/Cond.(Sign in to View) | Unit | Test Standard | Test Condition |
Tensile Modulus | ***/ *** | Mpa | ISO 527-2/1A | 1mm/min |
Tensile Strength | ||||
Break | ***/ *** | Mpa | ISO 527-2/1A | 5mm/min |
Tensile Elongation | ||||
Break | ***/ *** | % | ISO 527-2/1A | 5mm/min |
Flexural Modulus | ***/ *** | Mpa | ISO 178 | 2mm/min |
Flexural Strength | ||||
- | ***/ *** | Mpa | ISO 178 | 2mm/min |
| Impact | Dry/Cond.(Sign in to View) | Unit | Test Standard | Test Condition |
Charpy Notched Impact Strengh | ||||
23℃ (73℉) | ***/ *** | kJ/m² | ISO 179/1eA | Dry |
Charpy Unnotched Impact Strengh | ||||
-30℃ (-22℉) | ***/ *** | kJ/m² | ISO 179/1eU | Dry |
23℃ (73℉) | ***/ *** | kJ/m² | ISO 179/1eU | Dry |
| Thermal | Dry/Cond.(Sign in to View) | Unit | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | ||||
1.8 Mpa (264 psi)（18.6kg/cm²） | ***/ * | °C | ISO 75/Af | |
Melt Temperature(Tm) | ***/ * | °C | ISO 11357-1/-3 | 10°C/min |
| Flammability | Dry/Cond.(Sign in to View) | Unit | Test Standard | Test Condition |
Flame Rating | ||||
V-0 | ***/ * | mm | UL94 | |
5VA | ***/ * | mm | UL94 | |
Glow Wire Flammability Index(GWFI) | ||||
1mm | ***/ * | °C | IEC 60695-2-12 | |
2mm | ***/ * | °C | IEC 60695-2-12 | |
Glow Wire Ignition Test(GWIT) | ||||
1.0mm | ***/ * | °C | IEC 60695-2-13 | |
2.0mm | ***/ * | °C | IEC 60695-2-13 | |
| Electrical | Dry/Cond.(Sign in to View) | Unit | Test Standard | Test Condition |
Volume Resistivity | ***/ *** | Ohm-m | IEC 62631-3-1 | 500V |
Surface Resistivity | ***/ *** | Ohm | IEC 62631-3-2 | 500V |
Comparative Tracking Index (CTI) | ||||
Solution A | ***/ *** | V | IEC 60112 | |
Dielectric Strength | ***/ *** | kV/mm | IEC 60243-1 |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.