The product line Styrolux® comprises clear styrene butadiene copolymers. The grades have in general an intrinsic toughness, are easy to process and work as modifiers and compatibilizers not only in polystyrene but in many other polymers, e.g. polyolefins. For all Styrolux® grades food contact statements are available upon request. Styrolux® ECO 684D BC100 is a general purpose grade and can be used in injection molding for parts with enhanced toughness, in sheet and film extrusion as well as blow molding. Parts made of 684D reveal excellent printability. Styrolux ECO 684D BC100 is an ISCC compliant product leading to a substitution of fossil source styrene and butadiene with ISCC certified bio-attributed styrene and bio-attributed butadiene. This product exhibits a neutral to even negative carbon footprint.
FEATURES
- Easy processing
- Well extrudable
- Good printability
- Sterilisable(ETO,NO2,Irradiation)
- Transparency
APPLICATIONS
- Food contact applications
- Medical devices
- Rigid packaging
- Toys, sports & leisure
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 易成型良好的可印刷性生物基食品接触级射线灭菌环氧乙烷灭菌(EtO)二氧化氮灭菌 | |||
| 应用产品 | 食品包装包装玩具化妆品包装医疗器械体育用品休闲用品 | |||
| 颜色形状 | 粒状透明 | |||
| 成型方式 | 挤出片材挤出薄膜挤出 | |||
| 法规认证 | ISCC PLUS(国际可持续性和碳认证) | |||
| 曲线坐标点 | N粘度-剪切速度剪切应力-剪切速率应力-应变 (等时的) 23°C应力-应变 (等时的) 40°C应力-应变 (等时的) 60°C蠕变模量-时间 23°C蠕变模量-时间 40°C蠕变模量-时间 60°C | |||
| 生物基可再生 | 100% 是 | |||
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.01 g/cm³ | ISO 1183 | |
熔体体积流动速率(MVR) | |||
200°C/5.0 kg | 11 cm³/10 min | ISO 1133 | |
收缩率 | |||
- | 0.3~1 % | ISO 294-4 | |
吸水率 | 0.07 % | ISO 62 | Saturated at 23 °C |
回收料含量(PCR) | 100 % | Internal | |
碳足迹减少量 | 120 % | ISO 14044 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 26 Mpa | ISO 527 | 23 °C |
断裂(brk) | 21 Mpa | ISO 527 | 23 °C |
拉伸延伸率 | |||
屈服(yld) | 2.3 % | ISO 527 | 23 °C |
断裂(brk) | 160 % | ISO 527 | 23 °C |
标称断裂伸长率 | 160 % | ISO 527 | 23 °C |
弯曲强度 | |||
- | 40 Mpa | ISO 178 | 23 °C |
弯曲模量 | 1300 Mpa | ISO 178 | 23 °C |
拉伸模量 | 1400 Mpa | ISO 527 | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
23℃ (73℉) | 2 kJ/m² | ISO 179/1eA | |
简支梁无缺口(Charpy Unnotched) | |||
23℃ (73℉) | 80 kJ/m² | ISO 179/1eU | |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
邵氏硬度 D | 63 D | ISO 868 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 73 °C | ISO 75 | annealed 4 h/80 °C |
1.8 Mpa (264 psi)（18.6kg/cm²） | 59 °C | ISO 75 | annealed 4 h/80 °C |
维卡软化温度(Vicat) | 50 °C | ISO 306 | VST/B/50 (50N, 50 °C/h) |
线性膨胀系数(CLTE) | |||
- | 60~90 E-6/°C | ISO 11359 | |
加工温度 | 180~250 °C | - | |
模具温度 | 30~50 °C | - | |
| 光学性能 | 值/单位 | 测试标准 | 测试条件 |
透光率 | 89 % | ASTM D1003 | at 550 nm |
雾度 | 2 % | ASTM D1003 | |
折射率 | 1.58 - | ISO 489 | Sodium D Line |
此物性表中的信息由阿技材料库从该材料的生产商处获得。阿技材料库尽最大努力确保此数据的准确性。 但是阿技材料库对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。