Novodur® acrylonitrile butadiene styrene (ABS) polymers feature high surface quality and good impact strength. Novodur® ECO P2MC is an injection molding grade especially suitable for electroplating, providing high flowability. Novodur ECO P2MC BC50 is an ISCC compliant product leading to a substitution of fossil source styrene with ISCC certified bio-attributed styrene.
FEATURES
- Easy processing
- Designed for electroplating
APPLICATIONS
- Automotive exterior trim : mirror housings, exterior pillars & trims, spoilers
- Automotive electroplated parts
- Cosmetic packaging
- Shower heads
| 原厂资料 | 物性表(英文) | |||
| 树脂缩写 | ABS | |||
| 产品特性 | 良好冲击性易成型电镀/真空镀生物基高流动 | |||
| 应用产品 | 化妆品包装汽车外饰件汽车装饰件汽车立柱扰流板汽车后视镜外壳淋浴头 | |||
| 成型方式 | 注塑 | |||
| 法规认证 | ISCC PLUS(国际可持续性和碳认证) | |||
| 曲线坐标点 | N粘度-剪切速度剪切应力-剪切速率动态剪切模量 (G 储能)-温度比容-温度(pvT) | |||
| 生物基可再生 | 50% 是 | |||
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.03 g/cm³ | ISO 1183 | |
熔体体积流动速率(MVR) | |||
220°C/10.0 kg | 25 cm³/10 min | ISO 1133 | |
收缩率 | |||
- | 0.2~0.7 % | ISO 294-4 | |
生物基含量 | 50 % | - | min. |
碳足迹减少量 | 64 % | ISO 14044 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 40 Mpa | ISO 527 | 23 °C |
断裂(brk) | 31 Mpa | ISO 527 | 23 °C |
拉伸延伸率 | |||
屈服(yld) | 2.4 % | ISO 527 | 23 °C |
断裂(brk) | 15 % | ISO 527 | 23 °C |
标称断裂伸长率 | 16 % | ISO 527 | 23 °C |
弯曲强度 | |||
- | 62 Mpa | ISO 178 | 23 °C |
弯曲模量 | 2100 Mpa | ISO 178 | 23 °C |
拉伸模量 | 2200 Mpa | ISO 527 | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-30℃ (-22℉) | 16 kJ/m² | ISO 179/1eA | |
23℃ (73℉) | 25 kJ/m² | ISO 179/1eA | |
简支梁无缺口(Charpy Unnotched) | |||
23℃ (73℉) | 150 kJ/m² | ISO 179/1eU | |
悬臂梁缺口(Izod Notched) | |||
-30℃ (-22℉) | 16 kJ/m² | ISO 180/A | |
23℃ (73℉) | 25 kJ/m² | ISO 180/A | |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
球压硬度 | 107 Mpa | ISO 2039-1 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 96 °C | ISO 75 | annealed 4 h/80 °C |
1.8 Mpa (264 psi)（18.6kg/cm²） | 94 °C | ISO 75 | annealed 4 h/80 °C |
维卡软化温度(Vicat) | 98 °C | ISO 306 | VST/B/120 (50N, 120 °C/h) |
维卡软化温度(Vicat) | 96 °C | ISO 306 | VST/B/50 (50N, 50 °C/h) |
线性膨胀系数(CLTE) | |||
- | 100 E-6/°C | ISO 11359 | |
加工温度 | 230~260 °C | - | |
模具温度 | 60~80 °C | - | |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
HB | 1.5 mm | IEC 60695-11-10 | |
灼热丝可燃性指数(GWFI) | |||
2mm | 700 °C | IEC 60695-2-12 | |
燃烧速率 | 50 mm/min | ISO 3795 | 2.0 mm |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
相对漏电起痕指数(CTI ) | |||
- | 600 V | IEC 60112 | |
绝缘强度 | 37 kV/mm | IEC 60243-1 | Short Time, 1 mm |
此物性表中的信息由阿技材料库从该材料的生产商处获得。阿技材料库尽最大努力确保此数据的准确性。 但是阿技材料库对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。