Novodur® acrylonitrile butadiene styrene (ABS) polymers feature high surface quality and good impact strength. Novodur® ECO P2H-AT is a general purpose injection molding grade with enhanced chemical resistance and contains an antistatic additive.It is designed for best aesthetics: stable high gloss and smooth finish. Novodur ECO P2H-AT BC50 is an ISCC compliant product leading to a substitution of fossil source styrene with ISCC certified bio-attributed styrene.
FEATURES
- Balanced properties
- Easy processing
- Good paintability
- High gloss
APPLICATIONS
- Housings for electrical & electronic devices
- Electrical and electronic components, switches, house automation
- Coffee machines
- Vacuum cleaner housings
- Cosmetic packaging
| 原厂资料 | 物性表(英文) | |||
| 树脂缩写 | ABS | |||
| 产品特性 | 良好表面高光泽易涂装生物基耐化学性 | |||
| 添加助剂 | 抗静电剂 | |||
| 应用产品 | 电子电器化妆品包装外壳电子设备电源开关咖啡机吸尘器 | |||
| 成型方式 | 注塑 | |||
| 法规认证 | ISCC PLUS(国际可持续性和碳认证) | |||
| 曲线坐标点 | N粘度-剪切速度剪切应力-剪切速率动态剪切模量 (G 储能)-温度应力-应变正割模量-应变应力-应变 (等时的) 23°C应力-应变 (等时的) 40°C应力-应变 (等时的) 60°C应力-应变 (等时的) 80°C应力-应变 (等时的) 23°C蠕变模量-时间 40°C蠕变模量-时间 60°C蠕变模量-时间 80°C比容-温度(pvT) | |||
| 生物基可再生 | 50% 是 | |||
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.05 g/cm³ | ISO 1183 | |
熔体体积流动速率(MVR) | |||
220°C/10.0 kg | 37 cm³/10 min | ISO 1133 | |
收缩率 | |||
- | 0.4~0.7 % | ISO 294-4 | |
吸水率 | 0.95 % | ISO 62 | Saturated at 23°C |
生物基含量 | 50 % | - | min. |
碳足迹减少量 | 68 % | ISO 14044 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 44 Mpa | ISO 527 | 23 °C |
断裂(brk) | 32 Mpa | ISO 527 | 23 °C |
拉伸延伸率 | |||
屈服(yld) | 2.1 % | ISO 527 | 23 °C |
断裂(brk) | 15 % | ISO 527 | 23 °C |
标称断裂伸长率 | 18 % | ISO 527 | 23 °C |
弯曲强度 | |||
- | 70 Mpa | ISO 178 | 23 °C |
弯曲模量 | 2400 Mpa | ISO 178 | 23 °C |
拉伸模量 | 2500 Mpa | ISO 527 | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-30℃ (-22℉) | 8 kJ/m² | ISO 179/1eA | |
23℃ (73℉) | 18 kJ/m² | ISO 179/1eA | |
简支梁无缺口(Charpy Unnotched) | |||
-30℃ (-22℉) | 80 kJ/m² | ISO 179/1eU | |
23℃ (73℉) | 100 kJ/m² | ISO 179/1eU | |
悬臂梁缺口(Izod Notched) | |||
-30℃ (-22℉) | 9 kJ/m² | ISO 180/A | |
23℃ (73℉) | 18 kJ/m² | ISO 180/A | |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
球压硬度 | 110 Mpa | ISO 2039-1 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 97 °C | ISO 75 | annealed 4 h/80 °C |
1.8 Mpa (264 psi)（18.6kg/cm²） | 93 °C | ISO 75 | annealed 4 h/80 °C |
维卡软化温度(Vicat) | 100 °C | ISO 306 | VST/B/120 (50N, 120 °C/h) |
维卡软化温度(Vicat) | 98 °C | ISO 306 | VST/B/50 (50N, 50 °C/h) |
线性膨胀系数(CLTE) | |||
- | 90 E-6/°C | ISO 11359 | |
加工温度 | 230~260 °C | - | |
模具温度 | 60~80 °C | - | |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
HB | 1.5 mm | IEC 60695-11-10 | |
灼热丝可燃性指数(GWFI) | |||
2mm | 700 °C | IEC 60695-2-12 | |
燃烧速率 | 60 mm/min | ISO 3795 | 2.0 mm |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
相对漏电起痕指数(CTI ) | |||
- | 600 V | IEC 60112 | |
绝缘强度 | 34 kV/mm | IEC 60243-1 | Short Time, 1.0 mm |
绝缘强度 | 34 kV/mm | IEC 60243-1 | Short Time, 1.5 mm |
此物性表中的信息由阿技材料库从该材料的生产商处获得。阿技材料库尽最大努力确保此数据的准确性。 但是阿技材料库对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。