Luran® S acrylonitrile styrene acrylate (ASA) polymers feature high surface quality and good impact strength including enhanced colour fastness. The products deliver superior long-term performance when exposed to UV irradiation and additionally provide excellent chemical resistance. Luran® S ECO 778TE is an extrusion grade with enhanced heat resistance and best chemical resistance among the Luran S grades. Luran S ECO 778TE BC30 is an ISCC compliant product leading to a substitution of fossil source styrene with ISCC certified bio attributed styrene.
FEATURES
- Chemical resistance
- Well extrudable
- Heat resistance
- Long-term property retention
- UV resistance
APPLICATIONS
- PVC capstock for sheets, sidings, roof tiles, gardening equipment
- Extruded sheets & profiles
- Sidings and deckings
| 原厂资料 | 物性表(英文) | |||
| 树脂缩写 | ASA | |||
| 产品特性 | 耐热生物基抗紫外线耐候性耐化学性 | |||
| 应用产品 | 板材装饰板型材合成树脂板/瓦园林工具PVC表面共挤层围栏外墙装饰板 | |||
| 成型方式 | 挤出 | |||
| 法规认证 | ISCC PLUS(国际可持续性和碳认证) | |||
| 曲线坐标点 | 动态剪切模量 (G 储能)-温度应力-应变正割模量-应变应力-应变 (等时的) 23°C应力-应变 (等时的) 60°C蠕变模量-时间 23°C蠕变模量-时间 60°C比容-温度(pvT)拉伸模量-温度 | |||
| 生物基可再生 | 30% 是 | |||
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.07 g/cm³ | ISO 1183 | |
熔体体积流动速率(MVR) | |||
220°C/10.0 kg | 5 cm³/10 min | ISO 1133 | |
收缩率 | |||
- | 0.4~0.7 % | ISO 294-4 | |
吸水率 | 1.65 % | ISO 62 | Saturated at 23 °C |
吸湿率 | 0.35 % | ISO 62 | Equilibrium 23 °C/50% RH |
回收料含量(PCR) | 30 % | Internal | min. |
碳足迹减少量 | 39 % | ISO 14044 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 54 Mpa | ISO 527 | 23 °C |
拉伸延伸率 | |||
屈服(yld) | 3.4 % | ISO 527 | 23 °C |
标称断裂伸长率 | 8 % | ISO 527 | 23 °C |
弯曲强度 | |||
- | 80 Mpa | ISO 178 | 23 °C |
弯曲模量 | 2450 Mpa | ISO 178 | 23 °C |
拉伸模量 | 2500 Mpa | ISO 527 | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-30℃ (-22℉) | 4 kJ/m² | ISO 179/1eA | |
23℃ (73℉) | 15 kJ/m² | ISO 179/1eA | |
简支梁无缺口(Charpy Unnotched) | |||
23℃ (73℉) | 220 kJ/m² | ISO 179/1eU | |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
球压硬度 | 85 Mpa | ISO 2039-1 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 106 °C | ISO 75 | annealed 4 h/80 °C |
1.8 Mpa (264 psi)（18.6kg/cm²） | 103 °C | ISO 75 | annealed 4 h/80 °C |
维卡软化温度(Vicat) | 104 °C | ISO 306 | VST/B/50 (50N, 50 °C/h) |
线性膨胀系数(CLTE) | |||
- | 80~110 E-6/°C | ISO 11359 | |
导热系数 | 0.17 W/(m K) | ISO 22007 | |
加工温度 | 200~250 °C | - |
此物性表中的信息由阿技材料库从该材料的生产商处获得。阿技材料库尽最大努力确保此数据的准确性。 但是阿技材料库对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。