Luran® S acrylonitrile styrene acrylate (ASA) polymers feature high surface quality and good impact strength including enhanced colour fastness. The products deliver superior long-term performance when exposed to UV irradiation and additionally provide excellent chemical resistance. Luran® S ECO 778T is an injection molding grade with enhanced heat resistance and best chemical resistance among the Luran S grades. Luran S ECO 778T BC30 is an ISCC compliant product leading to a substitution of fossil source styrene with ISCC certified bio attributed styrene.
FEATURES
- Chemical resistance
- Heat resistance
- Long-term property retention
- UV resistance
APPLICATIONS
- Unpainted automotive exterior: radiator grills
- Truck: exterior body panels
- Bicycle/ E-bicycle parts
- Toys, sports & leisure
| 原厂资料 | 物性表(英文) | |||
| 树脂缩写 | ASA | |||
| 产品特性 | 耐热抗紫外线耐候性耐化学性 | |||
| 应用产品 | 散热器格栅重型卡车/货车汽车外室零件应用玩具散热器格栅重型卡车/货车汽车外室零件应用体育用品休闲用品自行车零部件电动自行车部件 | |||
| 成型方式 | 注塑 | |||
| 法规认证 | ISCC PLUS(国际可持续性和碳认证) | |||
| 曲线坐标点 | N粘度-剪切速度剪切应力-剪切速率动态剪切模量 (G 储能)-温度应力-应变正割模量-应变应力-应变 (等时的) 23°C应力-应变 (等时的) 60°C蠕变模量-时间 23°C蠕变模量-时间 60°C比容-温度(pvT)拉伸模量-温度 | |||
| 生物基可再生 | 30% 是 | |||
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.07 g/cm³ | ISO 1183 | |
熔体体积流动速率(MVR) | |||
220°C/10.0 kg | 5 cm³/10 min | ISO 1133 | |
收缩率 | |||
纵向(Flow) | 0.4~0.7 % | Internal | |
吸水率 | 1.65 % | ISO 62 | Saturated at 23 °C |
吸湿率 | 0.35 % | ISO 62 | Equilibrium 23 °C/50% RH |
回收料含量(PCR) | 30 % | Internal | min. |
碳足迹减少量 | 39 % | ISO 14044 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 54 Mpa | ISO 527 | 23 °C |
拉伸延伸率 | |||
屈服(yld) | 3.4 % | ISO 527 | 23 °C |
标称断裂伸长率 | 8 % | ISO 527 | 23 °C |
弯曲强度 | |||
- | 80 Mpa | ISO 178 | 23 °C |
弯曲模量 | 2450 Mpa | ISO 178 | 23 °C |
拉伸模量 | 2500 Mpa | ISO 527 | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-30℃ (-22℉) | 4 kJ/m² | ISO 179/1eA | |
23℃ (73℉) | 15 kJ/m² | ISO 179/1eA | |
简支梁无缺口(Charpy Unnotched) | |||
23℃ (73℉) | 220 kJ/m² | ISO 179/1eU | |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
球压硬度 | 85 Mpa | ISO 2039-1 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 106 °C | ISO 75 | annealed 4 h/80 °C |
1.8 Mpa (264 psi)（18.6kg/cm²） | 103 °C | ISO 75 | annealed 4 h/80 °C |
维卡软化温度(Vicat) | 104 °C | ISO 306 | VST/B/50 (50N, 50 °C/h) |
线性膨胀系数(CLTE) | |||
- | 80~110 E-6/°C | ISO 11359 | |
导热系数 | 0.17 W/(m K) | ISO 22007 | |
加工温度 | 240~280 °C | - | |
模具温度 | 40~80 °C | - | |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
HB | 1.5 mm | IEC 60695-11-10 | |
FMVSS | 30 mm/min | FMVSS 302 | 2.0 mm |
燃烧速率 | 30 mm/min | ISO 3795 | 2.0 mm |
此物性表中的信息由阿技材料库从该材料的生产商处获得。阿技材料库尽最大努力确保此数据的准确性。 但是阿技材料库对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。