ACRYMID® TT50 is a highly heat distortion-resistant poly(n-methyl methacrylimide) (PMMI). Besides showing the properties common to all ACRYMID® molding compounds, such as
• high heat deflection temperature under load,
• excellent transmission and clarity,
• very high strength and rigidity, as well as
• good weather resistance.
ACRYMID® TT50 is special in that it is
• listed by AMECA.
Application:
ACRYMID® molding compound is particularly suitable for injection molding of items meant for applications that involve high heat loads.
Examples: automotive lighting, light guides, lenses, fiber optics, luminaire covers, sight glasses, cover lenses.
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 耐热透光耐候性 | |||
| 应用产品 | 灯罩灯具透镜视窗防护盖板观察窗 | |||
| 成型方式 | 注塑 | |||
| 法规认证 | AMECA(美国加拿大汽车认证) | |||
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.21 g/cm³ | ISO 1183 | |
熔体体积流动速率(MVR) | |||
260°C/10 kg | 5 cm³/10 min | ISO 1133 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 80 Mpa | ISO 527 | 5 mm/min |
拉伸延伸率 | |||
断裂(brk) | 3 % | ISO 527 | 5 mm/min |
拉伸模量 | 4000 Mpa | ISO 527 | 1 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁无缺口(Charpy Unnotched) | |||
23℃ (73℉) | 20 kJ/m² | ISO 179/1eU | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 146 °C | ISO 75 | |
1.8 Mpa (264 psi)（18.6kg/cm²） | 142 °C | ISO 75 | |
维卡软化温度(Vicat) | 150 °C | ISO 306 | B / 50 |
线性膨胀系数(CLTE) | |||
- | 53 E-6/K | ISO 11359 | 0 - 50°C |
玻璃化温度(Tg) | 151 °C | ISO 11357 | |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
HB | 1.5 mm | IEC 60695-11-10 | |
| 光学性能 | 值/单位 | 测试标准 | 测试条件 |
透光率 | 91 % | ISO 13468-2 | 3 mm, D65 |
折射率 | 1.53 - | ISO 489 | 3 mm, 589nm/23°C |
此物性表中的信息由阿技材料库从该材料的生产商处获得。阿技材料库尽最大努力确保此数据的准确性。 但是阿技材料库对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。