Eltex® SuperstressTM TUB124N6000 is a high-density polyethylene copolymer designed for the extrusion of pressure pipes. It is classified PE 100 in accordance with ISO 12162 based on ISO 9080 analysis.
This PE100 compound providing a step-out performance of increased stress cracking resistance, is designed to allow maximum safety under all installation conditions and reduction of installation costs using no dig trenchless techniques or sandless laying
Characteristics
PE 100 blue pipe compound displaying
Outstanding resistance to stress cracking
Very good processability – ideal for thin layer coextrusion
Applications
Water
Relining technologies
Coextruded pipes
| Original Document | Technical Datasheet(English) | |||
| Features | Easy processingESCRCopolymer | |||
| Applications | Pressure PipesPipes/Tubes | |||
| Appearance | Pellets/GranulesBlue | |||
| Processing | ExtrusionCo-extrusion | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | |
Melt Mass Flow Rate(MFR) | |||
190℃/5 kg | *** g/10 min | ISO 1133 | |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ISO 527-2 | 23°C @ 1 mm/min |
Tensile Strength | |||
Yield | *** Mpa | ISO 527-2 | 23°C @ 50 mm/min |
Tensile Elongation | |||
Break | *** % | ISO 527-2 | 23°C @ 50 mm/min |
Notch Pipe Test | *** hr | ISO 13479 | 80°C and 9,2 bar |
FNCT | *** hr | ISO 16770 | 80°C, Arkopal N100, 4N/mm2 |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Vicat Softening Temperature(VST) | *** °C | ISO 306 | 1 kg |
| Additional Information | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Oxidative Induction Time | *** Min | ISO 11357 | 210°C |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.