Polyphthalamid with carbon fibers, natural color (black)
Main features
Very strong and stiff parts; low coefficient of thermal expansion. Low influence from moisture and temperature on dimensional stability and electrical properties, compared with PA66 Suitable for metal inserts. Improved friction and wear behaviour. Optimised for dry running operations.
| Original Document | Technical Datasheet(English) | |||
| Features | High StrengthHigh Stiffness/RigidityAnti-StaticWear/Abrasion ResistanceLow Friction/WearDimensional StabilityLow CLTELow Moisture AbsorptionFilled & Reinforced | |||
| Appearance | Pellets/GranulesBlack | |||
| Processing | Injection | |||
| Reinforced | Carbon Fiber | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | |
Mold Shrinkage | |||
Flow | *** % | ISO 294 | 60x60x2 mm |
Across Flow | *** % | ISO 294 | 60x60x2 mm |
Water Absorption | *** % | ISO 62 | 23°C / 24h |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ISO 527 | dry, @1 mm/min |
Tensile Strength | |||
- | *** Mpa | ISO 527 | dry, @50 mm/min |
Tensile Elongation | |||
Break | *** % | ISO 527 | dry, @50 mm/min |
Flexural Modulus | *** Mpa | ISO 178 | dry, @2 mm/min |
Flexural Strength | |||
- | *** Mpa | ISO 178 | dry, @10 mm/min |
Flexural Strain | |||
break | *** % | ISO 178 | dry, @10 mm/min |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
- | *** kJ/m² | ISO 179/1eA | dry |
Charpy Unnotched Impact Strengh | |||
- | *** kJ/m² | ISO 179/1eU | dry |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75/A | 80x10x4mm |
Continuous Use Temperature | |||
20000 hr | *** °C | IEC 60216 | |
| Electrical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Surface Resistivity | *** Ohm | IEC 62631-3-2 | ROB |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.