22% talc filled PP Homopolymer compound with high rigidity and offering low odour and low emissions performances.
| Original Document | Technical Datasheet(English) | |||
| Status | Commercial: Active | |||
| Availability | Europe | |||
| Features | High Stiffness/RigidityColor StabilityEasy processingLow EmissionLow OdorUV StabiltiyMedium FlowHomopolymerFilled & Reinforced | |||
| Applications | Automotive PartsAutomotive Instrument PanelAutomotive Interior Trims | |||
| Appearance | Pellets/GranulesBlack | |||
| Processing | Injection | |||
| Reinforced | 22% Talc | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | |
Melt Mass Flow Rate(MFR) | |||
230°C/2.16 kg | *** g/10min | ISO 1133 | |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Strength | |||
Yield | *** Mpa | ISO 527-1/-2 | 23 °C |
Flexural Modulus | *** Mpa | ISO 178 | 23 °C, Tech. A |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 179-1/1eA | |
23℃ (73℉) | *** kJ/m² | ISO 179-1/1eA | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ISO 75-1/-2 | Unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75-1/-2 | Unannealed |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.