| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Density/Specific Gravity |
*** g/cm³
| ISO 1183 | |
Mold Shrinkage | | | |
Flow |
*** % | Internal | 80×80×1mmt,pressure 60MPa |
Across Flow |
*** % | Internal | 80×80×1mmt,pressure 60MPa |
Water Absorption |
*** %
| ISO 62 | 23℃,24hrs,1mmt |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Strength | | | |
- |
*** Mpa | ASTM D 638 | |
Tensile Elongation | | | |
- |
*** % | ASTM D 638 | |
Flexural Modulus |
*** Mpa
| ISO 178 | |
Flexural Strength | | | |
- |
*** Mpa | ISO 178 | |
Flexural Strain | | | |
- |
*** % | ISO 178 | |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | | | |
23℃ (73℉) |
*** kJ/m² | ISO 179/1eA | |
| Hardness | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Rockwell M |
*** M
| ISO 2039-2 | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | | | |
0.45 Mpa (66 psi)（4.6kg/cm²） |
*** °C | ISO 75-1/-2 | |
1.8 Mpa (264 psi)（18.6kg/cm²） |
*** °C | ISO 75-1/-2 | |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Flame Rating | | | |
V-0 |
*** mm | UL94 | |
| Electrical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Volume Resistivity |
*** Ohm-cm
| IEC 60093 | |
Dielectric Constant(Permittivity) | | | |
1 kHz |
*** - | IEC 60250 | |
1MHz |
*** - | IEC 60250 | |
Dissipation Factor | | | |
1 kHz |
*** E-4 | IEC 60250 | |
1MHz |
*** E-4 | IEC 60250 | |
Comparative Tracking Index (CTI) | | | |
- |
*** V | IEC 60112 | |
Dielectric Strength |
*** kV/mm
| IEC 60243-1 | 1mmt |
Dielectric Strength |
*** kV/mm
| IEC 60243-1 | 3mmt |
Arc Resistance |
*** sec
| ASTM D495 | |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.