Hostacom HKG 424-3L E1 NAT is a 30% glass fiber reinforced PP homopolymer with medium melt flow.
The grade is UL listed in all colors as part of a family with 20, 30, 40 and 50% glass fiber loading and UL 2157 certified.
Hostacom HKG 424-3L E1 NAT has an RTI of 115°C.
| Original Document | Technical Datasheet(English) | |||
| Status | Commercial: Active | |||
| Availability | Europe | |||
| Features | Medium FlowHomopolymerFilled & Reinforced | |||
| Applications | Home appliances | |||
| Markets | Electrical / ElectronicsWhite Goods | |||
| Appearance | Pellets/GranulesNatural Color | |||
| Processing | Injection | |||
| Reinforced | 30% Glass Fiber | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | |
Density/Specific Gravity | *** g/cm³ | ASTM D792 | |
Melt Volume Flow Rate(MVR) | |||
230℃/2.16 kg | *** cm³/10 min | ISO 1133 | |
Melt Mass Flow Rate(MFR) | |||
230°C/2.16 kg | *** g/10min | ASTM D 1238 | |
230°C/2.16 kg | *** g/10min | ISO 1133 | |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** kg/cm² | ASTM D638 | 23 °C |
Tensile Modulus | *** Mpa | ISO 527-1/-2 | 23 °C |
Tensile Strength | |||
Break | *** Mpa | ISO 527-1/-2 | 23 °C |
- | *** kg/cm² | ASTM D 638 | 23 °C |
Tensile Elongation | |||
Break | *** % | ISO 527-1/-2 | 23 °C |
Flexural Modulus | *** kg/cm² | ASTM D790 | 23 °C |
Flexural Modulus | *** Mpa | ISO 178 | 23 °C, Tech. A |
Flexural Strength | |||
- | *** kg/cm² | ASTM D790 | 23 °C |
- | *** Mpa | ISO 178 | 23 °C, Tech. A |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
0℃ (32℉) | *** kJ/m² | ISO 179-1/1eA | |
23℃ (73℉) | *** kJ/m² | ISO 179-1/1eA | |
Charpy Unnotched Impact Strengh | |||
0℃ (32℉) | *** kJ/m² | ISO 179-1/1eU | |
23℃ (73℉) | *** kJ/m² | ISO 179-1/1eU | |
Izod Notched Impact Strengh | |||
23℃ (73℉) | *** kg·cm/cm | ASTM D256 | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ISO 75-1/-2 | Unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ASTM D648 | Unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75-1/-2 | Unannealed |
Vicat Softening Temperature(VST) | *** °C | ISO 306/B50 |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.