Hostacom GP621-2 medium melt flow, 3,000 MPa flexural modulus, 20% talc-filled polypropylene homopolymer is designed for high stiffness and good colorability.
| Original Document | Technical Datasheet(English) | |||
| Status | Commercial: Active | |||
| Availability | North America | |||
| Features | High Stiffness/RigidityGood ColoringEasy processingMedium FlowHomopolymerFilled & Reinforced | |||
| Appearance | Pellets/GranulesNatural Color | |||
| Processing | Injection | |||
| Reinforced | 20% Talc | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | Method A |
Melt Mass Flow Rate(MFR) | |||
230°C/2.16 kg | *** g/10min | ASTM D 1238 | |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Strength | |||
Yield | *** Mpa | ISO 527-1/-2 | 23 °C |
Tensile Elongation | |||
Yield | *** % | ISO 527-1/-2 | 23 °C |
Flexural Modulus | *** Mpa | ISO 178 | 23 °C |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Izod Notched Impact Strengh | |||
23℃ (73℉) | *** kJ/m² | ISO 180 | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ISO 75-1/-2 | Unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75-1/-2 | Unannealed |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.