| 原厂资料 | 物性表(英文) | |||
| 缩写标识 | PA66-GF25 FR(40) | |||
| 产品特性 | 阻燃无卤无红磷绝缘填充增强 | |||
| 添加助剂 | 阻燃剂脱模剂 | |||
| 应用行业 | 汽车行业电子电器 | |||
| 颜色形状 | 粒状黑色 | |||
| 成型方式 | 注塑 | |||
| 曲线坐标 | 应力-应变 -20|%|Mpa|Strain in %|Stress in MPa|0:0@0.141:13.6819@0.282:26.6144@0.423:38.7724@0.5641:50.1721@0.7050999999999999:60.8546@0.8461:70.8749@0.9871:80.29130000000001@1.1281:89.1571@1.2691:97.51600000000001@1.4101:105.398@1.5512:112.82@1.6922:119.785@1.8332:126.291@1.9742:132.329@2.1152:137.895@2.2562:142.996@2.3972:147.665@2.5382:151.973@2.6793:155.955{n}23|%|Mpa|Strain in %|Stress in MPa|0:0@0.1445:13.5699@0.2889:26.1154@0.4334:37.7745@0.5779:48.6404@0.7224:58.7744@0.8668:68.2182@1.0113:77.0018@1.1558:85.151@1.3003:92.69119999999999@1.4447:99.6507@1.5892:106.061@1.7337:111.953@1.8782:117.359@2.0226:122.3@2.1671:126.784@2.3116:130.797@2.4561:134.29@2.6005:137.169@2.745:139.056{n}90|%|Mpa|Strain in %|Stress in MPa|0:0@0.226:12.2061@0.4521:22.2051@0.6781:30.5468@0.9041:37.6487@1.1302:43.8164@1.3562:49.265@1.5822:54.1365@1.8083:58.5166@2.0343:62.4494@2.2603:65.95050000000001@2.4864:69.01909999999999@2.7124:71.64700000000001@2.9385:73.8292@3.1645:75.5697@3.3905:76.8879@3.6166:77.8233@3.8426:78.4395@4.0686:78.82689999999999@4.2947:78.9464{n}120|%|Mpa|Strain in %|Stress in MPa|0:0@0.2674:11.4098@0.5347:20.5292@0.8021:28.0085@1.0694:34.2965@1.3368:39.6917@1.6042:44.3795@1.8715:48.4672@2.1389:52.0227@2.4062:55.0884@2.6736:57.6976@2.9409:59.8854@3.2083:61.6944@3.4757:63.1757@3.743:64.38249999999999@4.0104:65.3629@4.2777:66.14570000000001@4.5451:66.72410000000001@4.8125:66.91249999999999@5.0798:67.0012{n}150|%|Mpa|Strain in %|Stress in MPa|0:0@0.2453:9.6067@0.4907:17.3576@0.736:23.7126@0.9813:29.0116@1.2267:33.4944@1.472:37.3283@1.7174:40.6263@1.9627:43.4665@2.208:45.9099@2.4534:47.9998@2.6987:49.7755@2.944:51.2741@3.1894:52.533@3.4347:53.5877@3.68:54.4676@3.9254:55.1911@4.1707:55.7551@4.416:56.1268@4.6614:56.2322{n}180|%|Mpa|Strain in %|Stress in MPa|0:0@0.2643:9.0396@0.5286:16.1547@0.793:21.8134@1.0573:26.3736@1.3216:30.0967@1.5859:33.1759@1.8502:35.7452@2.1145:37.9071@2.3789:39.7347@2.6432:41.2818@2.9075:42.5905@3.1718:43.6959@3.4361:44.6282@3.7004:45.412@3.9648:46.0649@4.2291:46.5927@4.4934:46.9847@4.7577:47.2055@5.022:47.1989应力-应变 (湿态) 23|%|Mpa|Strain in %|Stress in MPa|0:0@0.1559:11.6816@0.3119:22.5385@0.4678:32.3463@0.6238:41.0417@0.7796999999999999:48.6675@0.9357:55.3356@1.0916:61.1851@1.2476:66.36239999999999@1.4035:70.995@1.5595:75.1835@1.7154:78.9821@1.8714:82.4027@2.0273:85.41800000000001@2.1833:87.9708@2.3392:89.98779999999999@2.4952:91.4003@2.6511:92.1677@2.8071:92.3052{n}90|%|Mpa|Strain in %|Stress in MPa|0:0@0.226:9.553900000000001@0.452:17.5041@0.6778999999999999:24.2176@0.9039:29.966@1.1299:34.946@1.3559:39.2938@1.5819:43.1029@1.8078:46.4347@2.0338:49.3371@2.2598:51.8425@2.4858:53.9775@2.7118:55.7675@2.9377:57.2392@3.1637:58.4199@3.3897:59.3378@3.6157:60.0176@3.8417:60.4771@4.0676:60.7206@4.2936:60.713正割模量-应变 -20|%|MPa|Strain in %|Secant modulus in MPa|0.141:9703.48@0.282:9437.73@0.423:9166.049999999999@0.5641:8894.190000000001@0.7050999999999999:8630.629999999999@0.8461:8376.66@0.9871:8134.06@1.1281:7903.3@1.2691:7683.87@1.4101:7474.51@1.5512:7273.08@1.6922:7078.65@1.8332:6889.1@1.9742:6702.92@2.1152:6519.24@2.2562:6337.91@2.3972:6159.9@2.5382:5987.43@2.6793:5820.74{n}23|%|MPa|Strain in %|Secant modulus in MPa|0.1445:9390.93@0.2889:9039.6@0.4334:8715.85@0.5779:8416.75@0.7224:8135.99@0.8668:7870.12@1.0113:7614.14@1.1558:7367.28@1.3003:7128.45@1.4447:6897.67@1.5892:6673.86@1.7337:6457.46@1.8782:6248.48@2.0226:6046.67@2.1671:5850.4@2.3116:5658.29@2.4561:5467.61@2.6005:5274.72@2.745:5065.79{n}90|%|MPa|Strain in %|Secant modulus in MPa|0.226:5400.93@0.4521:4911.55@0.6781:4504.76@0.9041:4164.22@1.1302:3876.87@1.3562:3632.58@1.5822:3421.6@1.8083:3236@2.0343:3069.82@2.2603:2917.78@2.4864:2775.86@2.7124:2641.46@2.9385:2512.48@3.1645:2388.05@3.3905:2267.75@3.6166:2151.84@3.8426:2041.31@4.0686:1937.45@4.2947:1838.23{n}120|%|MPa|Strain in %|Secant modulus in MPa|0.2674:4266.94@0.5347:3839.39@0.8021:3491.9@1.0694:3207.08@1.3368:2969.16@1.6042:2766.46@1.8715:2589.75@2.1389:2432.22@2.4062:2289.44@2.6736:2158.05@2.9409:2036.3@3.2083:1922.96@3.4757:1817.64@3.743:1720.08@4.0104:1629.83@4.2777:1546.29@4.5451:1468.04@4.8125:1390.39@5.0798:1318.97{n}150|%|MPa|Strain in %|Secant modulus in MPa|0.2453:3916.31@0.4907:3537.31@0.736:3221.82@0.9813:2956.45@1.2267:2730.45@1.472:2535.89@1.7174:2365.57@1.9627:2214.63@2.208:2079.25@2.4534:1956.46@2.6987:1844.43@2.944:1741.65@3.1894:1647.11@3.4347:1560.19@3.68:1480.1@3.9254:1406@4.1707:1336.83@4.416:1270.99@4.6614:1206.34{n}180|%|MPa|Strain in %|Secant modulus in MPa|0.2643:3420.2@0.5286:3056.13@0.793:2750.74@1.0573:2494.43@1.3216:2277.29@1.5859:2091.93@1.8502:1931.96@2.1145:1792.72@2.3789:1670.3@2.6432:1561.81@2.9075:1464.85@3.1718:1377.64@3.4361:1298.8@3.7004:1227.22@3.9648:1161.85@4.2291:1101.72@4.4934:1045.64@4.7577:992.192@5.022:939.843正割模量-应变 (湿态) 23|%|MPa|Strain in %|Secant modulus in MPa|0.1559:7493.01@0.3119:7226.19@0.4678:6914.56@0.6238:6579.3@0.7796999999999999:6241.82@0.9357:5913.82@1.0916:5605.08@1.2476:5319.21@1.4035:5058.43@1.5595:4821@1.7154:4604.3@1.8714:4403.27@2.0273:4213.39@2.1833:4029.26@2.3392:3846.95@2.4952:3663.05@2.6511:3476.58@2.8071:3288.28{n}90|%|MPa|Strain in %|Secant modulus in MPa|0.226:4227.39@0.452:3872.59@0.6778999999999999:3572.44@0.9039:3315.19@1.1299:3092.84@1.3559:2897.99@1.5819:2724.76@1.8078:2568.57@2.0338:2425.86@2.2598:2294.12@2.4858:2171.43@2.7118:2056.48@2.9377:1948.44@3.1637:1846.57@3.3897:1750.53@3.6157:1659.92@3.8417:1574.23@4.0676:1492.79@4.2936:1414.03比容-温度(pvT) 30|°C|E-3 m³/kg|Spec. volume in °C|Temperature in E-3 m³/kg|27:0.72451@47:0.72756@67:0.73066@87:0.73382@107:0.73711@127:0.74059@147:0.7444@167:0.74876@187:0.754@207:0.7607@217:0.76488@222:0.76725@227:0.76983@232:0.7726499999999999@237:0.7757500000000001@238:0.77641@239:0.77708@241:0.78004@242:0.7805@277:0.79648@300:0.80682{n}60|°C|E-3 m³/kg|Spec. volume in °C|Temperature in E-3 m³/kg|27:0.71884@47:0.72183@67:0.7248599999999999@87:0.72794@107:0.73112@127:0.73443@147:0.73799@167:0.74194@187:0.74655@207:0.75224@217:0.75569@227:0.75971@232:0.76198@237:0.76445@242:0.76715@243:0.76772@244:0.7683@246:0.77039@252:0.77289@277:0.78318@300:0.7924600000000001{n}90|°C|E-3 m³/kg|Spec. volume in °C|Temperature in E-3 m³/kg|27:0.71362@47:0.71657@67:0.71955@87:0.72256@107:0.72564@127:0.72883@147:0.73219@167:0.73585@187:0.73999@207:0.74492@227:0.75116@237:0.75503@242:0.7572@247:0.75957@248:0.76007@249:0.76058@250:0.76109@252:0.76248@257:0.76439@277:0.77195@300:0.78044{n}120|°C|E-3 m³/kg|Spec. volume in °C|Temperature in E-3 m³/kg|27:0.70879@47:0.7117@67:0.71463@87:0.71759@107:0.7206@127:0.7236900000000001@147:0.7269@167:0.73034@187:0.73412@207:0.7385@227:0.74383@237:0.74704@247:0.75076@252:0.75285@254:0.75374@255:0.75419@257:0.75518@262:0.75695@267:0.75872@277:0.76222@300:0.77012线性热膨胀系数(CTE)-温度 αn|°C|%|Temperature in °C|ΔL/L0 in %|-50:-0.46379@-40:-0.40456@-30:-0.35002@-20:-0.28702@-10:-0.22907@0:-0.16035@10:-0.09696@20:-0.02521@30:0.04494@40:0.13189@50:0.22458@60:0.3304@70:0.44823@80:0.56086@90:0.6934900000000001@100:0.81789@110:0.94247@120:1.06649@130:1.19384@140:1.32521@150:1.44554{n}αp|°C|%|Temperature in °C|ΔL/L0 in %|-50:-0.18009@-40:-0.15889@-30:-0.13471@-20:-0.10966@-10:-0.08647000000000001@0:-0.06049@10:-0.03621@20:-0.009639999999999999@30:0.01428@40:0.03986@50:0.06113@60:0.08007@70:0.09668@80:0.11462@90:0.13157@100:0.14818@110:0.16413@120:0.17908@130:0.19303@140:0.20699@150:0.21928拉伸模量-温度 |°C|MPa|Temperature in °C|Tensile modulus in MPa|-20:9525@23:9100@85:5115@120:4130@150:3800@180:3300 | |||
| 增强填充 | 25% 玻纤 | |||
| 物理性能 | 值/单位(登录后可见) | 测试标准 | 测试条件 |
|---|---|---|---|
密度/比重 | *** g/cm³ | ISO 1183 | Dry |
收缩率 | |||
纵向(Flow) | *** % | ISO 294-4 | 280°C Melt Temp, 80°C Mold Temp, 60 MPa Cavity Press |
横向(Across Flow) | *** % | ISO 294-4 | 280°C Melt Temp, 80°C Mold Temp, 60 MPa Cavity Press |
吸水率 | *** % | ISO 62 | immersion at 23°C, 2mm thk |
吸湿率 | *** % | ISO 62 | 23°C – 50%RH, 2mm thk |
| 机械性能 | 值/单位(登录后可见) | 测试标准 | 测试条件 |
拉伸模量 | *** Mpa | ISO 527-2/1A | Dry, 1mm/min |
拉伸强度 | |||
断裂(brk) | *** Mpa | ISO 527-2/1A | Dry, 5mm/min |
拉伸延伸率 | |||
断裂(brk) | *** % | ISO 527-2/1A | Dry, 5mm/min |
弯曲模量 | *** Mpa | ISO 178 | Dry, 2mm/min |
弯曲强度 | |||
- | *** Mpa | ISO 178 | Dry, 2mm/min |
| 冲击性能 | 值/单位(登录后可见) | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
23℃ (73℉) | *** kJ/m² | ISO 179/1eA | Dry |
简支梁无缺口(Charpy Unnotched) | |||
23℃ (73℉) | *** kJ/m² | ISO 179/1eU | Dry |
| 热学性能 | 值/单位(登录后可见) | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
1.8 Mpa (264 psi)(18.6kg/cm²) | *** °C | ISO 75-2/Af | |
维卡软化温度(Vicat) | *** °C | ISO 306/B50 | 50°C/h, 50N |
线性膨胀系数(CLTE) | |||
纵向(Flow) | *** E-6/K | ISO 11359-1/-2 | 23°C – 55°C |
横向(Across Flow) | *** E-6/K | ISO 11359-1/-2 | 23°C – 55°C |
熔融温度(Tm) | *** °C | ISO 11357-1/-3 | 10°C/min |
| 燃烧性能 | 值/单位(登录后可见) | 测试标准 | 测试条件 |
防火等级 | |||
V-0 | *** mm | UL94 | |
5VA | *** mm | UL94 | |
灼热丝可燃性指数(GWFI) | |||
1mm | *** °C | IEC 60695-2-12 | |
2mm | *** °C | IEC 60695-2-12 | |
灼热丝点燃温度(GWIT) | |||
1.0mm | *** °C | IEC 60695-2-13 | |
2.0mm | *** °C | IEC 60695-2-13 | |
燃烧速率 | mm/min | ASTM D 635 | 3mm |
| 电学性能 | 值/单位(登录后可见) | 测试标准 | 测试条件 |
体积电阻率 | *** Ohm-m | IEC 60093 | Cond., 500V |
体积电阻率 | *** Ohm-m | IEC 60093 | Dry,500V |
表面电阻率 | *** Ohm | IEC 60093 | Cond., 500V |
表面电阻率 | *** Ohm | IEC 60093 | Dry,500V |
相对漏电起痕指数(CTI) | |||
溶液A | *** - | IEC 60112 |
此物性表中的信息由阿技材料库从该材料的生产商处获得。阿技材料库尽最大努力确保此数据的准确性。 但是阿技材料库对这些数据值不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。
| 中文名 | 英文名 | 文件格式 | 操作 |
|---|---|---|---|
| 物性表(英文) | Technical Datasheet(English) | 下载 |
| 供应商 | 价格 | 地区 | 留言 | 联系方式 |
|---|
| 分类 | 值 |
|---|