PA66 flame retardant for injection molding, halogens and red phosphorus free. reinforced with 25% glass fiber. Black Colour.
Suitable for parts requiring properties to flame retardants, medium stiffness and good resistance mechanics. Good electrical insulation properties. Ranked V-0 according to UL-94.
| Original Document | Technical Datasheet(English) | |||
| Resin ID | PA66-GF25 FR(40) | |||
| Features | Flame RetardantHalogen FreeNon Red PhosphorusInsulatingFilled & Reinforced | |||
| Additive | Flame RetardantRelease Agent | |||
| Markets | AutomotiveElectrical / Electronics | |||
| Appearance | Pellets/GranulesBlack | |||
| Processing | Injection | |||
| Diagrams | Stress-strainStress-strain (Cond.)Secant modulus-strainSecant modulus-strain (Cond.)Specific volume-temperature (pvT)Coefficient of Linear Thermal Expansion(CTE)-TemperatureTensile modulus-temperature | |||
| Reinforced | 25% Glass Fiber | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | Dry |
Mold Shrinkage | |||
Flow | *** % | ISO 294-4 | 280°C Melt Temp, 80°C Mold Temp, 60 MPa Cavity Press |
Across Flow | *** % | ISO 294-4 | 280°C Melt Temp, 80°C Mold Temp, 60 MPa Cavity Press |
Water Absorption | *** % | ISO 62 | immersion at 23°C, 2mm thk |
Moisture /Humidity Absorption | *** % | ISO 62 | 23°C – 50%RH, 2mm thk |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ISO 527-2/1A | Dry, 1mm/min |
Tensile Strength | |||
Break | *** Mpa | ISO 527-2/1A | Dry, 5mm/min |
Tensile Elongation | |||
Break | *** % | ISO 527-2/1A | Dry, 5mm/min |
Flexural Modulus | *** Mpa | ISO 178 | Dry, 2mm/min |
Flexural Strength | |||
- | *** Mpa | ISO 178 | Dry, 2mm/min |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
23℃ (73℉) | *** kJ/m² | ISO 179/1eA | Dry |
Charpy Unnotched Impact Strengh | |||
23℃ (73℉) | *** kJ/m² | ISO 179/1eU | Dry |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75-2/Af | |
Vicat Softening Temperature(VST) | *** °C | ISO 306/B50 | 50°C/h, 50N |
Coefficient of Linear Thermal Expansion | |||
Flow | *** E-6/K | ISO 11359-1/-2 | 23°C – 55°C |
Across Flow | *** E-6/K | ISO 11359-1/-2 | 23°C – 55°C |
Melt Temperature(Tm) | *** °C | ISO 11357-1/-3 | 10°C/min |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Flame Rating | |||
V-0 | *** mm | UL94 | |
5VA | *** mm | UL94 | |
Glow Wire Flammability Index(GWFI) | |||
1mm | *** °C | IEC 60695-2-12 | |
2mm | *** °C | IEC 60695-2-12 | |
Glow Wire Ignition Test(GWIT) | |||
1.0mm | *** °C | IEC 60695-2-13 | |
2.0mm | *** °C | IEC 60695-2-13 | |
Burning Rate | mm/min | ASTM D 635 | 3mm |
| Electrical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Volume Resistivity | *** Ohm-m | IEC 60093 | Cond., 500V |
Volume Resistivity | *** Ohm-m | IEC 60093 | Dry,500V |
Surface Resistivity | *** Ohm | IEC 60093 | Cond., 500V |
Surface Resistivity | *** Ohm | IEC 60093 | Dry,500V |
Comparative Tracking Index (CTI) | |||
Solution A | *** - | IEC 60112 |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.