Glass fibre reinforced, heat aging resistant injection moulding grade for industrial articles.
| Original Document | Technical Datasheet(English) | |||
| Solutions | Automotive connectors - A. Raymond | |||
| Resin ID | PA610-GF30 | |||
| Availability | Europe | |||
| Features | Good Heat AgingFilled & Reinforced | |||
| Appearance | Pellets/GranulesBlack | |||
| Processing | Injection | |||
| Technical Notes | Tensile Strength-Time(Heat Resistant Aging)(in media) | |||
| Diagrams | Stress-strainStress-strain (Cond.)Secant modulus-strainSecant modulus-strain (Cond.)Coefficient of Linear Thermal Expansion(CTE)-Temperature | |||
| Reinforced | 30% Glass Fiber | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | |
Melt Volume Flow Rate(MVR) | |||
275°C/5 kg | *** cm³/10 min | ISO 1133 | |
Mold Shrinkage | |||
Flow | *** % | ISO 294-4 | |
Across Flow | *** % | ISO 294-4 | |
Water Absorption | *** % | ISO 62 | saturation in water at 23°C |
Moisture /Humidity Absorption | ***~*** % | ISO 62 | equilibrium 23°C/50% r.h. |
Viscosity | *** cm³/g | ISO 307, 1157, 1628 | 0.5% in 96% H2SO4 |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ISO 527-1/-2 | Cond. |
Tensile Modulus | *** Mpa | ISO 527-1/-2 | Dry |
Tensile Strength | |||
Break | *** Mpa | ISO 527-1/-2 | Cond. |
Break | *** Mpa | ISO 527-1/-2 | Dry |
Tensile Elongation | |||
Break | *** % | ISO 527-1/-2 | Cond. |
Break | *** % | ISO 527-1/-2 | Dry |
Flexural Modulus | *** Mpa | ISO 178 | Cond. |
Flexural Modulus | *** Mpa | ISO 178 | Dry |
Flexural Strength | |||
- | *** Mpa | ISO 178 | Cond. |
- | *** Mpa | ISO 178 | Dry |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 179/1eA | Cond. |
-30℃ (-22℉) | *** kJ/m² | ISO 179/1eA | Dry |
23℃ (73℉) | *** kJ/m² | ISO 179/1eA | Cond. |
23℃ (73℉) | *** kJ/m² | ISO 179/1eA | Dry |
Charpy Unnotched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 179/1eU | Cond. |
-30℃ (-22℉) | *** kJ/m² | ISO 179/1eU | Dry |
23℃ (73℉) | *** kJ/m² | ISO 179/1eU | Cond. |
23℃ (73℉) | *** kJ/m² | ISO 179/1eU | Dry |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ISO 75-1/-2 | |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75-1/-2 | |
Vicat Softening Temperature(VST) | *** °C | ISO 306/B50 | 50 N, 50 K/h |
Specific Heat | *** J/kg-K | - | |
Coefficient of Linear Thermal Expansion | |||
Flow | *** E-6/K | ISO 11359-1/-2 | (23-55)°C |
Across Flow | *** E-6/K | ISO 11359-1/-2 | (23-55)°C |
Melt Temperature(Tm) | *** °C | ISO 11357-1/-3 | DSC |
Thermal Conductivity | *** W/(m K) | DIN 52612-1 | |
Processing Temperature | ***~*** °C | - | Injection moulding/Extrusion |
Mould temperature | ***~*** °C | - | Injection moulding |
| Electrical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Volume Resistivity | *** Ohm-m | IEC 62631-3-1 | Cond. |
Volume Resistivity | *** Ohm-m | IEC 62631-3-1 | Dry |
Surface Resistivity | *** Ohm | IEC 62631-3-2 | Cond. |
Dielectric Constant(Permittivity) | |||
1MHz | *** - | IEC 62631-2-1 | Cond. |
1MHz | *** - | IEC 62631-2-1 | Dry |
Dissipation Factor | |||
1MHz | *** E-4 | IEC 62631-2-1 | Cond. |
1MHz | *** E-4 | IEC 62631-2-1 | Dry |
Comparative Tracking Index (CTI) | |||
Solution A | *** V | IEC 60112 |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.