Polyphthalamide, light colorable, with a high melting point, halogen-free flame-retardant, very low water absorption, good mechanical and dielectrical properties at elevated temperatures as well as excellent chemical resistance, soldering bath resistant. Colors available (e.g. Orange RAL 2003).
Markets & applications
Automotive: Automotive electrics & electronics (E&E), sensors, fuel cell, e-mobility
E&E: Connectors, SMT (surface mount technology) applications, energy distribution
Consumer goods: Home appliances, consumer electronics, cell phone parts
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | |
Melt Volume Flow Rate(MVR) | |||
325°C/5.0 kg | *** cm³/10 min | ISO 1133 | |
Mold Shrinkage | |||
Flow | *** % | ISO 294-4 | |
Across Flow | *** % | ISO 294-4 | |
Water Absorption | ***~*** % | ISO 62 | saturation in water at 23°C |
Moisture /Humidity Absorption | ***~*** % | ISO 62 | equilibrium 23°C/50% r.h. |
Viscosity | *** cm³/g | ISO 307, 1157, 1628 | 0.5% in 96% H2SO4 |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ISO 527-1/-2 | Cond., 23°C |
Tensile Modulus | *** Mpa | ISO 527-1/-2 | Dry, 120°C |
Tensile Modulus | *** Mpa | ISO 527-1/-2 | Dry, 23°C |
Tensile Strength | |||
Break | *** Mpa | ISO 527-1/-2 | Cond., 23°C |
Break | *** Mpa | ISO 527-1/-2 | Dry, 23°C |
Tensile Elongation | |||
Break | *** % | ISO 527-1/-2 | Cond., 23°C |
Break | *** % | ISO 527-1/-2 | Dry, 23°C |
Flexural Modulus | *** Mpa | ISO 178 | Cond., 23°C |
Flexural Modulus | *** Mpa | ISO 178 | Dry, 23°C |
Flexural Strength | |||
- | *** Mpa | ISO 178 | Cond. |
- | *** Mpa | ISO 178 | Dry |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
23℃ (73℉) | *** kJ/m² | ISO 179/1eA | Cond. |
23℃ (73℉) | *** kJ/m² | ISO 179/1eA | Dry |
Charpy Unnotched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 179/1eU | Dry |
23℃ (73℉) | *** kJ/m² | ISO 179/1eU | Cond. |
23℃ (73℉) | *** kJ/m² | ISO 179/1eU | Dry |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75-1/-2 | |
Coefficient of Linear Thermal Expansion | |||
Flow | *** E-6/K | ISO 11359-1/-2 | (23-55)°C |
Across Flow | *** E-6/K | ISO 11359-1/-2 | (23-55)°C |
Melt Temperature(Tm) | *** °C | ISO 11357-1/-3 | DSC |
Processing Temperature | ***~*** °C | - | Injection moulding/Extrusion |
Processing Temperature | *** °C | - | Test specimen production |
Mould temperature | ***~*** °C | - | Injection moulding |
Mould temperature | *** °C | - | Test specimen production |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Flame Rating | |||
V-0 | *** mm | UL94 | |
V-0 | *** mm | IEC 60695-11-10 | |
V-0 | *** mm | IEC 60695-11-10 | |
Glow Wire Flammability Index(GWFI) | |||
1mm | *** °C | IEC 60695-2-12 | |
Glow Wire Ignition Test(GWIT) | |||
1.0mm | *** °C | IEC 60695-2-13 | |
| Electrical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Volume Resistivity | *** Ohm-m | IEC 62631-3-1 | Cond. |
Volume Resistivity | *** Ohm-m | IEC 62631-3-1 | Dry |
Surface Resistivity | *** Ohm | IEC 62631-3-2 | Cond. |
Comparative Tracking Index (CTI) | |||
Solution A | *** V | IEC 60112 | Cond. |
Dielectric Strength | *** kV/mm | IEC 60243-1 | Cond., K20/K20, (60*60*1 mm³) |
Dielectric Strength | *** kV/mm | IEC 60243-1 | Dry, K20/K20, (60*60*1 mm³) |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.