Preliminary Product - Ultramid Advanced N3HC4 is a 20% short carbon fiber reinforced grade of PA9T. This product is naturally black in color due to the carbon reinforcement.
Markets & applications
Automotive: Metal replacement, structural parts for body, chassis and powertrain, lightweight parts
Industry goods: Loaded industrial equipment, pumps, fans, gears and compressors
Consumer goods: Thin precision structures in consumer electronics
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 填充增强 | |||
| 应用产品 | 金属替代高应力部件轻量化部件精密部件 | |||
| 颜色形状 | 粒状黑色 | |||
| 成型方式 | 注塑 | |||
| 增强填充 | 20% 碳纤 | |||
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.225 g/cm³ | ISO 1183 | |
收缩率 | |||
纵向(Flow) | 0.26 % | ISO 294-4 | |
横向(Across Flow) | 0.7 % | ISO 294-4 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 283 Mpa | ISO 527-1/-2 | Cond. |
断裂(brk) | 288 Mpa | ISO 527-1/-2 | Dry |
拉伸延伸率 | |||
断裂(brk) | 2.2 % | ISO 527-1/-2 | Cond. |
断裂(brk) | 2.1 % | ISO 527-1/-2 | Dry |
弯曲强度 | |||
- | 396 Mpa | ISO 178 | Cond. |
- | 404 Mpa | ISO 178 | Dry |
弯曲模量 | 18100 Mpa | ISO 178 | Cond. |
弯曲模量 | 18000 Mpa | ISO 178 | Dry |
拉伸模量 | 19700 Mpa | ISO 527-1/-2 | Cond. |
拉伸模量 | 19900 Mpa | ISO 527-1/-2 | Dry |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-40℃ (-40℉) | 8.6 kJ/m² | ISO 179/1eA | Dry |
23℃ (73℉) | 9.3 kJ/m² | ISO 179/1eA | Dry |
简支梁无缺口(Charpy Unnotched) | |||
23℃ (73℉) | 76 kJ/m² | ISO 179/1eU | Dry |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | 287 °C | ISO 75-1/-2 | |
熔融温度(Tm) | 300 °C | ISO 11357-1/-3 | DSC |
加工温度 | 310~350 °C | - | Injection moulding/Extrusion |
模具温度 | 80~160 °C | - | Injection moulding |
此物性表中的信息由阿技材料库从该材料的生产商处获得。阿技材料库尽最大努力确保此数据的准确性。 但是阿技材料库对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。