Ultramid® 8202 HS BK102 is a heat stabilized, low viscosity, general purpose Polyamid 6 injection molding. It possesses the combination of strength and toughness and has excellent chemical and abrasion resistance. The heat stabilizer system extends the retention of properties at the more elevated temperatures. Excellent in filling thin walls or areas.
Ultramid® 8202 HS is generally recommended for drapery hardware, gears, fittings, furniture casters, bearings, handles, clips, fasteners and thin parts.
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 高强度高韧性热稳定耐磨耐化学性低粘度 | |||
| 添加助剂 | 热稳定剂 | |||
| 应用产品 | 夹子紧固件齿轮轴承家具脚轮 | |||
| 成型方式 | 注塑 | |||
| 汽车材料 | 福特(FORD) WSK-M4D672-A通用(GM) GMW17173P-PA6斯泰兰蒂斯(Stellantis) MS-DB-41 | |||
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.13 g/cm³ | ISO 1183 | |
吸水率 | 9.5 % | ISO 62 | saturation in water at 23°C |
吸湿率 | 2.7 % | ISO 62 | equilibrium 23°C/50% r.h. |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 36 Mpa | ISO 527-1/-2 | Cond., 50 mm/min |
屈服(yld) | 85 Mpa | ISO 527-1/-2 | Dry, 50 mm/min |
拉伸延伸率 | |||
屈服(yld) | 16 % | ISO 527-1/-2 | Cond., 50 mm/min |
屈服(yld) | 4 % | ISO 527-1/-2 | Dry, 50 mm/min |
标称断裂伸长率 | 50 % | ISO 527-1/-2 | Cond., 50 mm/min |
标称断裂伸长率 | 25 % | ISO 527-1/-2 | Dry, 50 mm/min |
拉伸模量 | 970 Mpa | ISO 527-1/-2 | Cond., 50 mm/min |
拉伸模量 | 3100 Mpa | ISO 527-1/-2 | Dry |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
23℃ (73℉) | 3 kJ/m² | ISO 179/1eA | Dry |
简支梁无缺口(Charpy Unnotched) | |||
23℃ (73℉) | NB kJ/m² | ISO 179/1eU | Dry |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | 60 °C | ISO 75-1/-2 | |
熔融温度(Tm) | 220 °C | ISO 11357-1/-3 | DSC |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
V-2 | 0.7 mm | IEC 60695-11-10 | |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 1.0E+13 Ohm-m | IEC 62631-3-1 | Dry |
此物性表中的信息由阿技材料库从该材料的生产商处获得。阿技材料库尽最大努力确保此数据的准确性。 但是阿技材料库对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。