Ultradur® B1520 FC R01 UN is suitable for plastic parts, where material approval regarding drinking water contact and direct food contact is a mandatory requirement.
The product is approved according to
· 21 CFR FDA §177.1660 "Poly(tetramethylene terephthalate)";
· European Food Contact European Food Contact Commission Regulation (EU) 10/2011;
· GMP (EC) N°2023/2006
| Original Document | Technical Datasheet(English) | |||
| Resin ID | PBT | |||
| Features | Food ContactDrinking Water Contact | |||
| Compliance | EU 2011/10/ECFDA | |||
| Diagrams | Shearstress-shear rateViscosity-shear rate | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | |
Melt Volume Flow Rate(MVR) | |||
250℃/2.16 kg | *** cm³/10 min | ISO 1133 | |
Mold Shrinkage | |||
Flow | *** % | ISO 294-4 | |
Across Flow | *** % | ISO 294-4 | |
Water Absorption | *** % | ISO 62 | equilibrium in water at 23°C |
Moisture /Humidity Absorption | *** % | ISO 62 | equilibrium 23°C/50% r.h. |
Viscosity | *** cm³/g | ISO 307, 1157, 1628 | solution 0,005 g/ml Phenole/1,2 Dichlorbenzol 1:1 |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ISO 527-1/-2 | |
Tensile Strength | |||
Yield | *** Mpa | ISO 527-1/-2 | 50 mm/min |
Tensile Elongation | |||
Yield | *** % | ISO 527-1/-2 | 50 mm/min |
Nominal Tensile Strain at Break | *** % | ISO 527-1/-2 | 50 mm/min |
Flexural Strength | |||
- | *** Mpa | ISO 178 | |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
23℃ (73℉) | *** kJ/m² | ISO 179/1eA | |
Charpy Unnotched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 179/1eU | |
23℃ (73℉) | *** kJ/m² | ISO 179/1eU | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ISO 75-1/-2 | |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75-1/-2 | |
Vicat Softening Temperature(VST) | *** °C | ISO 306/B50 | 50 N, 50 K/h |
Vicat Softening Temperature(VST) | *** °C | ISO 306/A50 | 10 N, 50 K/h |
Specific Heat | *** J/kg-K | - | |
Coefficient of Linear Thermal Expansion | |||
Flow | *** E-6/K | ISO 11359-1/-2 | (23-55)°C |
Across Flow | *** E-6/K | ISO 11359-1/-2 | (23-55)°C |
Melt Temperature(Tm) | *** °C | ISO 11357-1/-3 | DSC |
Processing Temperature | ***~*** °C | - | Injection moulding/Extrusion |
Mould temperature | ***~*** °C | - | Injection moulding |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.