High viscosity extrusion grade with improved hydrolysis resistance and an exceptionally high melt strength for the extrusion of loose buffer tubes, profiles, hollow rods, pipes and blow molded parts.
| Original Document | Technical Datasheet(English) | |||
| Features | Hydrolysis ResistanceHigh ViscosityHigh melt strength | |||
| Appearance | Pellets/GranulesNatural Color | |||
| Processing | ExtrusionProfile ExtrusionBlow Molding | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | |
Melt Volume Flow Rate(MVR) | |||
250℃/2.16 kg | *** cm³/10 min | ISO 1133 | |
Mold Shrinkage | |||
Flow | *** % | ISO 294-4 | |
Across Flow | *** % | ISO 294-4 | |
Viscosity | *** cm³/g | ISO 307, 1157, 1628 | solution 0,005 g/ml Phenole/1,2 Dichlorbenzol 1:1 |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ISO 527-1/-2 | |
Tensile Strength | |||
Yield | *** Mpa | ISO 527-1/-2 | 50 mm/min |
Tensile Elongation | |||
Yield | *** % | ISO 527-1/-2 | 50 mm/min |
Nominal Tensile Strain at Break | *** % | ISO 527-1/-2 | 50 mm/min |
Flexural Modulus | *** Mpa | ISO 178 | |
Flexural Strength | |||
- | *** Mpa | ISO 178 | |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 179/1eA | |
23℃ (73℉) | *** kJ/m² | ISO 179/1eA | |
Charpy Unnotched Impact Strengh | |||
23℃ (73℉) | *** kJ/m² | ISO 179/1eU | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75-1/-2 | |
Coefficient of Linear Thermal Expansion | |||
Flow | *** E-6/K | ISO 11359-1/-2 | (23-55)°C |
Across Flow | *** E-6/K | ISO 11359-1/-2 | (23-55)°C |
Melt Temperature(Tm) | *** °C | ISO 11357-1/-3 | DSC |
| Film | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Water Vapor Transmission Rate | *** g/m²/24 hr | ASTM F 1249 | 23°C, 85%RH |
Oxygen permeability | *** cm³*µm/(m²* d*bar) | ASTM F1927 | 23°C, 85%RH |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.