Ultradur® B6560M2 FC TF UN is suitable for plastic parts, where material approval regarding drinking water contact and direct food contact is a mandatory requirement.
The product is approved according to
· 21 CFR FDA §177.1660 "Poly(tetramethylene terephthalate)";
· European Food Contact European Food Contact Commission Regulation (EU) 10/2011;
· GMP (EC) N°2023/2006
| Original Document | Technical Datasheet(English) | |||
| Features | Food ContactDrinking Water ContactFilled & Reinforced | |||
| Compliance | EU 2011/10/ECFDA | |||
| Reinforced | 10% Mineral | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | |
Melt Volume Flow Rate(MVR) | |||
250℃/2.16 kg | *** cm³/10 min | ISO 1133 | |
Viscosity | *** cm³/g | ISO 307, 1157, 1628 | solution 0,005 g/ml Phenole/1,2 Dichlorbenzol 1:1 |
Bulk(Apparent ) Density | *** g/cm³ | ISO 60 | |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ISO 527-1/-2 | |
Tensile Strength | |||
Yield | *** Mpa | ISO 527-1/-2 | 50 mm/min |
Break | *** Mpa | ISO 527-1/-2 | |
Tensile Elongation | |||
Yield | *** % | ISO 527-1/-2 | 50 mm/min |
Nominal Tensile Strain at Break | *** % | ISO 527-1/-2 | 50 mm/min |
Flexural Modulus | *** Mpa | ISO 178 | |
Flexural Strength | |||
- | *** Mpa | ISO 178 | |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 179/1eA | |
23℃ (73℉) | *** kJ/m² | ISO 179/1eA | |
Charpy Unnotched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 179/1eU | |
23℃ (73℉) | *** kJ/m² | ISO 179/1eU | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ISO 75-1/-2 | |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75-1/-2 | |
Specific Heat | *** J/kg-K | - | |
Coefficient of Linear Thermal Expansion | |||
Flow | *** E-6/K | ISO 11359-1/-2 | (23-55)°C |
Across Flow | *** E-6/K | ISO 11359-1/-2 | (23-55)°C |
Melt Temperature(Tm) | *** °C | ISO 11357-1/-3 | DSC |
Processing Temperature | ***~*** °C | - | Injection moulding/Extrusion |
Mould temperature | ***~*** °C | - | Injection moulding |
| Electrical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Comparative Tracking Index (CTI) | |||
Solution A | *** V | IEC 60112 | |
| Film | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Water Vapor Transmission Rate | *** g/m²/24 hr | ASTM F 1249 | 23°C, 85%RH |
Oxygen permeability | *** cm³*µm/(m²* d*bar) | ASTM F1927 | 23°C, 50%RH |
Oxygen permeability | *** cm³*µm/(m²* d*bar) | ASTM F1927 | 23°C, 85%RH |
Oxygen permeability | *** cm³*µm/(m²* d*bar) | ASTM F1927 | 38°C, 90%RH |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.