BD265MO is a very high impact heterophasic copolymer based on proprietary Borstar Nucleation Technology (BNT). This product exhibits excellent impact strength even at low temperatures and good processability and stiffness properties.
Articles produced with this grade exhibit very good demoulding properties and dimensional consistency with respect to different colours.
| Original Document | Technical Datasheet(English) | |||
| Features | High ImpactHigh Impact at Low TemperaturDimensional StabilityEasy processingMold Release | |||
| Processing | Injection | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | ***~*** g/cm³ | ISO 1183 | |
Melt Mass Flow Rate(MFR) | |||
230°C/2.16 kg | *** g/10min | ISO 1133 | |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ISO 527-2 | 1 mm/min |
Tensile Strength | |||
Yield | *** Mpa | ISO 527-2 | 50 mm/min |
Tensile Elongation | |||
Yield | *** % | ISO 527-2 | 50 mm/min |
Flexural Modulus | *** Mpa | ISO 178 | |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 179/1eA | |
-20℃ (-4℉) | *** kJ/m² | ISO 179/1eA | |
23℃ (73℉) | *** kJ/m² | ISO 179/1eA | |
Izod Notched Impact Strengh | |||
-20℃ (-4℉) | *** J/m | ASTM D256 | |
23℃ (73℉) | *** J/m | ASTM D256 | |
| Hardness | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Rockwell R | *** R | ISO 2039-2 | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ISO 75-2 | |
Vicat Softening Temperature(VST) | *** °C | ISO 306/A |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.