Description
-Metallocene-catalyzed polypropylene homopolymer
-Outstanding organoleptic property (very low VOCs)
Application
-Compounding base resin for automotive part with low TVOC
| Original Document | Technical Datasheet-ASTM(English) | |||
| Features | Low EmissionHomopolymer | |||
| Applications | Compounding/BlendingAutomotive Parts | |||
| Processing | InjectionCompounding | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ASTM D 1505 | |
Melt Mass Flow Rate(MFR) | |||
230°C/2.16 kg | *** g/10min | ASTM D 1238 | |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Strength | |||
Yield | *** kg/cm² | ASTM D638 | 50mm/min |
Tensile Elongation | |||
Break | *** % | ASTM D638 | 50mm/min |
Flexural Modulus | *** kg/cm² | ASTM D790 | 1% Secant, Press sheet |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Izod Notched Impact Strengh | |||
23℃ (73℉) | *** kg·cm/cm | ASTM D256 | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ASTM D648 |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.