Description
It is designed for large sized injection molding with high flowability and special processing property.
Application
Chair
Key Features
Good Mold Release, High Flow, High Transparency, Weather Resistance
| Original Document | Technical Datasheet-ASTM(English) | |||
| Features | High TransparencyMold ReleaseWeather ResistanceHigh Flow | |||
| Applications | Chairs | |||
| Appearance | Pellets/GranulesClear/Transparent | |||
| Processing | Injection | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ASTM D792 | |
Melt Mass Flow Rate(MFR) | |||
300℃/1.2 kg | *** g/10min | ASTM D1238 | |
Mold Shrinkage | |||
- | ***~*** % | ASTM D955 | |
Water Absorption | *** % | ASTM D570 | 24 hrs, 23°C |
Water Absorption | *** % | ASTM D570 | equilibrium, 50%RH, 23°C |
Abrasion resistance | *** % | ASTM D 1044 | Taber, D Haze |
Spiral Flow | *** mm | - | |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ASTM D638 | |
Tensile Strength | |||
Yield | *** Mpa | ASTM D638 | |
Break | *** Mpa | ASTM D638 | |
Tensile Elongation | |||
Yield | *** % | ASTM D638 | |
Break | *** % | ASTM D638 | |
Flexural Modulus | *** Mpa | ASTM D790 | |
Flexural Strength | |||
- | *** Mpa | ASTM D790 | |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Izod Notched Impact Strengh | |||
23℃ (73℉) | *** J/m | ASTM D256 | |
Izod Unnotched Impact Strengh | |||
23℃ (73℉) | *** J/m | ASTM D256 | |
Instrumented Impact Energy | |||
23℃ (73℉)Total Energy | *** J | ASTM D3763 | |
| Hardness | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Rockwell M | *** M | ASTM D 785 | |
Rockwell R | *** R | ASTM D785 | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ASTM D648 | 4 mm, annealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ASTM D648 | 4 mm, annealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ASTM D648 | 4 mm, unannealed |
Vicat Softening Temperature(VST) | *** °C | ASTM D1525 | 50°C /hr, 50N Load |
Coefficient of Linear Thermal Expansion | |||
- | *** E-6/°C | ASTM D 696 | -40 to 82°C |
Ball Pressure Test | *** °C | IEC 598-1 | |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Flame Rating | |||
V-2 | ***~*** mm | ASTM D635 | |
Oxygen Index | *** % | ASTM D 2863 | |
Glow Wire Ignition Test(GWIT) | |||
2.0mm | *** °C | IEC 695-2-1 | 5 second |
Burning Rate | *** mm | ASTM D 635 | |
| Electrical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Volume Resistivity | *** Ohm-cm | ASTM D257 | 23 °C, dry |
Dielectric Constant(Permittivity) | |||
60 Hz | *** - | ASTM D 150 | |
Dissipation Factor | |||
60 Hz | *** E-4 | ASTM D 150 | |
Comparative Tracking Index (CTI) | |||
- | *** V | IEC 112 | 2.0 mm |
Dielectric Strength | *** kV/mm | ASTM D149 | |
| Optical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Light Transmission | *** % | ASTM D1003 | |
Haze | ***~*** % | ASTM D1003 | |
Refractive Index | *** - | ASTM D542 | nD |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.