Description
It is designed for compounding of PC alloy with high impact strength(low temp.) and excellent ESCR property.
Application
Compound
Key Features
Chemical Resistance, High Impact Resistance, Low Haze, Low Temp. Impact Resistance
| 原厂资料 | 物性表-ASTM(英文) | |||
| 产品特性 | 高冲击耐低温冲击ESCR耐化学性 | |||
| 应用产品 | 共混 | |||
| 成型方式 | 共混改性 | |||
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.2 g/cm³ | ASTM D792 | |
熔体质量流动速率(MFR) | |||
300℃/1.2 kg | 7 g/10min | ASTM D1238 | |
收缩率 | |||
- | 0.5~0.7 % | ASTM D 955 | |
吸水率 | 0.12 % | ASTM D570 | 24 hrs, 23°C |
吸水率 | 0.2 % | ASTM D570 | equilibrium, 50%RH, 23°C |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 56 Mpa | ASTM D638 | |
断裂(brk) | 66 Mpa | ASTM D638 | |
拉伸延伸率 | |||
屈服(yld) | 6 % | ASTM D638 | |
断裂(brk) | 100 % | ASTM D638 | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 640 J/m | ASTM D256 | |
悬臂梁无缺口(Izod Unnotched) | |||
23℃ (73℉) | NB J/m | ASTM D256 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 122 °C | ASTM D648 | 4 mm, annealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 108 °C | ASTM D648 | 4 mm, annealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 120 °C | ASTM D648 | 4 mm, unannealed |
维卡软化温度(Vicat) | 128 °C | ASTM D1525 | 50°C /hr, 50N Load |
线性膨胀系数(CLTE) | |||
- | 70 E-6/°C | ASTM D 696 | -40 to 82°C |
| 光学性能 | 值/单位 | 测试标准 | 测试条件 |
雾度 | 0~2 % | ASTM D1003 |
此物性表中的信息由阿技材料库从该材料的生产商处获得。阿技材料库尽最大努力确保此数据的准确性。 但是阿技材料库对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。