Description
It is designed for injection molding, compounding with ultra-high flowability and excellent coloring property.
Application
Compound, CD,DVD, E&E Others
Key Features
Coloring, High Transparency, Ultra High Flow
| 原厂资料 | 物性表-ASTM(英文) | |||
| 产品特性 | 高透明度易着色高流动 | |||
| 应用产品 | 共混电子电器CD盒DVD | |||
| 颜色形状 | 粒状透明 | |||
| 成型方式 | 注塑共混改性 | |||
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.2 g/cm³ | ASTM D792 | |
熔体质量流动速率(MFR) | |||
300℃/1.2 kg | 70 g/10min | ASTM D1238 | |
收缩率 | |||
- | 0.5~0.7 % | ASTM D 955 | |
吸水率 | 0.15 % | ASTM D570 | 24 hrs, 23°C |
吸水率 | 0.32 % | ASTM D570 | equilibrium, 50%RH, 23°C |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 60 Mpa | ASTM D638 | |
断裂(brk) | 48 Mpa | ASTM D638 | |
拉伸延伸率 | |||
屈服(yld) | 6 % | ASTM D638 | |
断裂(brk) | 60 % | ASTM D638 | |
弯曲强度 | |||
- | 100 Mpa | ASTM D790 | |
弯曲模量 | 2500 Mpa | ASTM D790 | |
拉伸模量 | 2300 Mpa | ASTM D638 | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 270 J/m | ASTM D256 | |
仪器化落镖冲击能量 | |||
23℃ (73℉)总能量 | 59 J | ASTM D3763 | |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
洛氏硬度 M | 58 M | ASTM D 785 | |
洛氏硬度R | 124 R | ASTM D785 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 137 °C | ASTM D648 | 4 mm, annealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 124 °C | ASTM D648 | 4 mm, unannealed |
维卡软化温度(Vicat) | 147 °C | ASTM D1525 | 50°C /hr, 50N Load |
线性膨胀系数(CLTE) | |||
- | 68 E-6/°C | ASTM D 696 | -40 to 82°C |
| 光学性能 | 值/单位 | 测试标准 | 测试条件 |
透光率 | 91 % | ASTM D1003 | |
折射率 | 1.583 - | ASTM D542 | nD |