LI928 is high flow and high heat ASA, engineered for parts with complex designs
Key Features
Standard Purpose, Non Painting, Superior Surface Quality, High Flow
Application
Bumper,Exterior ETC,Outside Mirror,Spoiler
| Original Document | Technical Datasheet-ASTM(English) Technical Datasheet-ISO(English) | |||
| Features | Heat ResistanceGood SurfacePaint-freeWeather ResistanceHigh Flow | |||
| Applications | Automotive Exterior TrimsBumper productsOutside MirrorSpoiler | |||
| Processing | Injection | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | 23℃ |
Density/Specific Gravity | *** g/cm³ | ASTM D792 | 23℃ |
Melt Mass Flow Rate(MFR) | |||
220℃/10 kg | *** g/10 min | ISO 1133 | |
220℃/10 kg | *** g/10 min | ASTM D 1238 | |
Mold Shrinkage | |||
- | ***~*** % | ASTM D955 | 23℃, 3.2mm |
- | ***~*** % | ISO 294-4 | 23℃, 3.2mm |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ASTM D638 | 23℃, 50mm/min, 3.2mm |
Tensile Modulus | *** Mpa | ISO 527 | 23℃,1mm/min, 4mm |
Tensile Strength | |||
Yield | *** Mpa | ASTM D638 | 23℃, 50mm/min, 3.2mm |
Yield | *** Mpa | ISO 527 | 23℃, 50mm/min, 4mm |
Tensile Elongation | |||
Break | *** % | ASTM D638 | 23℃, 50mm/min, 3.2mm |
Break | *** % | ISO 527 | 23℃, 50mm/min, 4mm |
Flexural Modulus | *** Mpa | ASTM D790 | 23℃, 10mm/min, 6.4mm |
Flexural Modulus | *** Mpa | ISO 178 | 23℃, 2mm/min, 4mm |
Flexural Strength | |||
- | *** Mpa | ASTM D790 | 23℃, 10mm/min, 6.4mm |
- | *** Mpa | ISO 178 | 23℃, 2mm/min, 4mm |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 179/1eA | 4mm |
23℃ (73℉) | *** kJ/m² | ISO 179/1eA | 4mm |
Izod Notched Impact Strengh | |||
-30℃ (-22℉) | *** J/m | ASTM D256 | 3.2mm |
-30℃ (-22℉) | *** J/m | ASTM D256 | 6.4mm |
-30℃ (-22℉) | *** kJ/m² | ISO 180/1A | 4mm |
23℃ (73℉) | *** J/m | ASTM D256 | 3.2mm |
23℃ (73℉) | *** J/m | ASTM D256 | 6.4mm |
23℃ (73℉) | *** kJ/m² | ISO 180/1A | 4mm |
| Hardness | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Rockwell R | *** R | ASTM D785 | |
Rockwell R | *** R | ISO 2039-2 | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ASTM D648 | 6.4mm, Annealed |
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ASTM D648 | 6.4mm, Unannealed |
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ISO 75 | 4mm, Annealed |
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ISO 75 | 4mm, Unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ASTM D648 | 6.4mm, Annealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ASTM D648 | 6.4mm, Unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75 | 4mm, Annealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75 | 4mm, Unannealed |
Vicat Softening Temperature(VST) | *** °C | ASTM D1525 | 50N, 50℃/h |
Vicat Softening Temperature(VST) | *** °C | ISO 306 | 50N, 50℃/h |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.