LI945-A is a high toughness and high heat ASA designed for metallized rear lamp housings
Key Features
High Heat Resistance, Non Painting, Weatherability, Metallization, High Stiffness
| Original Document | Technical Datasheet-ASTM(English) Technical Datasheet-ISO(English) | |||
| Features | High Stiffness/RigidityGood ToughnessHeat ResistanceMetal PlatingPaint-freeWeather Resistance | |||
| Applications | Rear Lamp Housings | |||
| Appearance | Pellets/GranulesClear/Transparent | |||
| Processing | Injection | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | 23℃ |
Melt Mass Flow Rate(MFR) | |||
220℃/10 kg | *** g/10 min | ISO 1133 | |
Mold Shrinkage | |||
- | ***~*** % | ISO 294-4 | 23℃, 3.2mm |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Strength | |||
Yield | *** Mpa | ISO 527 | 23℃, 50mm/min, 4mm |
Tensile Elongation | |||
Yield | *** % | ISO 527 | 23℃, 50mm/min, 4mm |
Break | *** % | ISO 527 | 23℃, 50mm/min, 4mm |
Flexural Modulus | *** Mpa | ISO 178 | 23℃, 2mm/min, 4mm |
Flexural Strength | |||
- | *** Mpa | ISO 178 | 23℃, 2mm/min, 4mm |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
23℃ (73℉) | *** kJ/m² | ISO 179/1eA | 4mm |
| Hardness | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Rockwell R | *** R | ISO 2039 | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75 | 4mm, Unannealed |
| Optical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Light Transmission | *** % | ASTM D1003 | 3.2mm |
Haze | *** % | ASTM D1003 |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.