Lotrene FD0274 is mainly recommended for the extrusion of thin film for light and medium duty applications.lt contains both slip additives (target 600 ppm erucamide) and anti blocking additives (target 900 ppm) as well asantioxidants.
PROPERTIES
The molecular structure of Lotrene@ FD0274 makes it possible to produce very thin, clear and glossy films.
APPLICATIONS
-Thin transparent film
-Thin shrink film
-Foam products
-Food packaging
-Deep Freeze
-Lamination film
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 高光泽食品接触级 | |||
| 添加助剂 | 抗氧化剂增滑剂开口剂 | |||
| 应用产品 | 食品包装复合膜收缩膜发泡产品 | |||
| 成型方式 | 薄膜挤出 | |||
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 0.923 g/cm³ | ASTM D792 | |
熔体质量流动速率(MFR) | |||
- | 2.4 g/10min | ASTM D1238 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
摩擦系数 | 0.12 - | Internal | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
维卡软化温度(Vicat) | 89 °C | ASTM D1525 | |
结晶温度 | 108 °C | Internal | |
| 光学性能 | 值/单位 | 测试标准 | 测试条件 |
雾度 | 8 % | ASTM D1003 | 40 µm, Blown Film |
光泽度 | 59 - | ASTM D 2457 | 45°, 40 µm, Blown Film |
| 薄膜性能 | 值/单位 | 测试标准 | 测试条件 |
薄膜测试厚度 | 40 μm | Internal | Blown Film |
拉伸强度 | |||
屈服(yld) | 11 Mpa | ASTM D 882 | MD |
屈服(yld) | 11 Mpa | ASTM D 882 | TD |
断裂(brk) | 24 Mpa | ASTM D 882 | MD |
断裂(brk) | 22 Mpa | ASTM D 882 | TD |
拉伸延伸率 | |||
断裂(brk) | 300 % | ASTM D 882 | MD |
断裂(brk) | 600 % | ASTM D 882 | TD |
穿透强度 | 30 N | Internal | |
埃尔曼多夫撕裂 | 65 N/mm | ASTM D 1922 | MD |
埃尔曼多夫撕裂 | 35 N/mm | ASTM D 1922 | TD |
落锤冲击 | 110 g | ASTM D 1709 | F50 |
此物性表中的信息由阿技材料库从该材料的生产商处获得。阿技材料库尽最大努力确保此数据的准确性。 但是阿技材料库对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。