Lotrène® Q3018C is a Linear Low Density Polyethylene resin produced in a gas phase reactor using butene (C4) co-monomer.
Lotrène® Q3018C is a cast film extrusion grade.
Lotrène® Q3018C can be processed at high output rates with good web stability and gauge control on cast film machines designed for LLDPE. Lotrène® Q3018C can advantageously be blended with LDPE or other PE resins used in cast film mono extrusion or co - extrusion to improve film properties .
| Original Document | Technical Datasheet(English) | |||
| Features | Food Contact | |||
| Applications | FilmCompounding/Blending | |||
| Processing | Cast FilmCo-extrusionCompounding | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ASTM D792 | |
Melt Mass Flow Rate(MFR) | |||
190℃/2.16 kg | *** g/10min | ASTM D1238 | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Vicat Softening Temperature(VST) | *** °C | ASTM D1525 | A120 |
Freezing temperature | *** °C | Internal | |
| Optical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Haze | *** % | ASTM D1003 | 20 µm, Cast Film |
Gloss | *** - | ASTM D 2457 | 45°, 20 µm, Cast Film |
| Film | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tested Film Thickness | *** μm | Internal | Cast Film |
Tensile Strength | |||
Yield | *** Mpa | ASTM D 882 | MD |
Yield | *** Mpa | ASTM D 882 | TD |
Break | *** Mpa | ASTM D 882 | MD |
Break | *** Mpa | ASTM D 882 | TD |
Tensile Elongation | |||
Break | *** % | ASTM D 882 | MD |
Break | *** % | ASTM D 882 | TD |
Piercing strength | *** N | ASTM D5748 | |
Puncture resistance | *** J | ASTM D 5748 | |
Elmondorf Tear | *** N/mm | ASTM D 1922 | MD |
Elmondorf Tear | *** N/mm | ASTM D 1922 | TD |
Secant Modulus | *** Mpa | ASTM D 882 | MD,1% Secant |
Secant Modulus | *** Mpa | ASTM D 882 | TD, 1% Secant |
Dart Drop Impact | *** g | ASTM D 1709 | F50 |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.