Polypropylene Aceso PPM H350 is homopolymer with a Melt Flow Index of 35 g/10 min recommended for the manufacture of medical packaging and medical devices, to the exclusion of implants.
Polypropylene Aceso PPM H350 is characterized by high fluidity and is particularly suitable for injection moulding applications. The material provides a good balance between stiffness and impact.
| Original Document | Technical Datasheet(English) | |||
| Features | Medical Application/Health CareHigh FlowHomopolymer | |||
| Processing | Injection | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | |
Melt Mass Flow Rate(MFR) | |||
230°C/2.16 kg | *** g/10min | ISO 1133 | |
Bulk(Apparent ) Density | *** g/cm³ | ISO 1183 | |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ISO 527-2 | |
Tensile Strength | |||
Yield | *** Mpa | ISO 527-2 | |
Tensile Elongation | |||
Yield | *** % | ISO 527-2 | |
Flexural Modulus | *** Mpa | ISO 178 | |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
23℃ (73℉) | *** kJ/m² | ISO 179 | |
Izod Notched Impact Strengh | |||
23℃ (73℉) | *** kJ/m² | ISO 180 | |
| Hardness | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Rockwell R | *** R | ISO 2039-2 | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ISO 75 | 120°C per hour |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75 | 120°C per hour |
Vicat Softening Temperature(VST) | *** °C | ISO 306 | 10N-50°C per hour |
Vicat Softening Temperature(VST) | *** °C | ISO 306 | 50N-50°C per hour |
Melt Temperature(Tm) | *** °C | ISO 3146 |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.