Polypropylene PPH 2060 is a homopolymer with a high molecular weight and a Melt Flow Index of 0.9 g/10 min.
PPH 2060 is particularly intended for the extrusion of pipes and sheets for industrial and civil engineering applications. The resin has a long-term stabilization package. It offers a high stiffness and good processability. Polypropylene PPH 2060 is available in natural color.
| Original Document | Technical Datasheet(English) | |||
| Features | High Stiffness/RigidityEasy processingHomopolymer | |||
| Appearance | Pellets/GranulesNatural Color | |||
| Processing | ExtrusionSheet ExtrusionTube Extrusion | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | |
Melt Mass Flow Rate(MFR) | |||
230°C/2.16 kg | *** g/10min | ISO 1133 | |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Strength | |||
Yield | *** Mpa | ISO 527-2 | |
Tensile Elongation | |||
Yield | *** % | ISO 527-2 | |
Break | *** % | ISO 527-2 | |
Flexural Modulus | *** Mpa | ISO 178 | |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
23℃ (73℉) | *** kJ/m² | ISO 179 | |
Izod Notched Impact Strengh | |||
23℃ (73℉) | *** kJ/m² | ISO 180 | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ISO 75 | 120°C per hour |
Vicat Softening Temperature(VST) | *** °C | ISO 306 | 10N-50°C per hour |
Vicat Softening Temperature(VST) | *** °C | ISO 306 | 50N-50°C per hour |
Melt Temperature(Tm) | *** °C | ISO 3146 |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.