Flame resistant Polycarbonate injection moulding grade; flame retardant without Halogens and without red phosphorus
| Original Document | Technical Datasheet(German) | |||
| Features | Flame RetardantHalogen FreeNon Red Phosphorus | |||
| Additive | Flame Retardant | |||
| Processing | Injection | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | 23°C |
Melt Volume Flow Rate(MVR) | |||
300°C/1.2 kg | *** cm³/10 min | ISO 1133 | |
Moisture /Humidity Absorption | *** % | ISO 62 | 23°C, 50% r.h. |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ISO 527-1/-2 | 23°C, 1 mm/Min |
Tensile Strength | |||
Yield | *** Mpa | ISO 527-1/-2 | 23°C, 50mm/Min |
Tensile Elongation | |||
Yield | *** % | ISO 527-1/-2 | 23°C, 50mm/Min |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
23℃ (73℉) | *** kJ/m² | ISO 179/1eA | |
Charpy Unnotched Impact Strengh | |||
23℃ (73℉) | *** kJ/m² | ISO 179/1eU | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ISO 75-1/-2 | |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75-1/-2 | |
Vicat Softening Temperature(VST) | *** °C | ISO 306/A50 | |
Continuous Use Temperature | |||
20000 hr | *** °C | IEC 60216 | |
Long term | *** °C | IEC 60216 | some hours |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Flame Rating | |||
V-0 | *** mm | UL94 | |
V-0 | *** mm | UL94 | |
Glow Wire Flammability Index(GWFI) | |||
2mm | *** °C | IEC 60695-2-12 | |
| Electrical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Comparative Tracking Index (CTI) | |||
- | *** V | IEC 60112 | |
Dielectric Strength | *** kV/mm | IEC 60243-1 |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.