Heat-stabilized, 30% carbon fibre reinforced injection moulding grade based on a partially aromatic polyphthalamide and PA66
| Original Document | Technical Datasheet(English) | |||
| Features | Heat StabilizedFilled & Reinforced | |||
| Additive | Heat Stabilizer | |||
| Processing | Injection | |||
| Reinforced | 30% Carbon Fiber | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | Dry |
Water Absorption | *** % | ISO 62 | 23°C, Saturation |
Moisture /Humidity Absorption | *** % | ISO 62 | 23°C, 50% r.h. |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ISO 527-1/-2 | Cond. |
Tensile Modulus | *** Mpa | ISO 527-1/-2 | Dry, 23°C, 1 mm/Min |
Tensile Strength | |||
Break | *** Mpa | ISO 527-1/-2 | Cond. |
Break | *** Mpa | ISO 527-1/-2 | Dry, 23°C, 5mm/Min |
Tensile Elongation | |||
Break | *** % | ISO 527-1/-2 | Cond. |
Break | *** % | ISO 527-1/-2 | Dry, 23°C, 5mm/Min |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
23℃ (73℉) | *** kJ/m² | ISO 179/1eA | Dry |
Charpy Unnotched Impact Strengh | |||
23℃ (73℉) | *** kJ/m² | ISO 179/1eU | Cond. |
23℃ (73℉) | *** kJ/m² | ISO 179/1eU | Dry |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75-1/-2 | |
Melt Temperature(Tm) | ***~*** °C | ISO 3146 | 10 K/min |
Continuous Use Temperature | |||
20000 hr | *** °C | IEC 60216 | |
Long term | *** °C | IEC 60216 | some hours |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Flame Rating | |||
HB | *** mm | UL94 | |
HB | *** mm | UL94 | |
| Electrical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Volume Resistivity | *** Ohm-cm | IEC 62631-3-1 | Dry |
Surface Resistivity | *** Ohm | IEC 62631-3-2 | Dry |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.